Robust and orange-yellow-emitting Sr-rich polytypoid α-SiAlON (Sr3Si24Al6N40:Eu2+) phosphor for white LEDs
Mehdi Estili,Rong-Jun Xie,Kohsei Takahashi,Shiro Funahashi,Tohru S. Suzuki,Naoto Hirosaki
DOI: https://doi.org/10.1080/14686996.2024.2396276
IF: 7.821
2024-09-21
Science and Technology of Advanced Materials
Abstract:Nitrides and oxynitrides isostructural to α-Si 3 N 4 ( M -α-SiAlON, M = Sr, Ca, Li) possess superb thermally stable photoluminescence (PL) properties, making them reliable phosphors for high-power solid-state lighting. However, the synthesis of phase-pure Sr-α-SiAlON still remains a great challenge and has only been reported for Sr below 1.35 at.% as the large size of Sr 2+ ions tends to destabilize the α-SiAlON structure. Here, we succeeded to synthesize the single-phase powders of a unique 'Sr-rich' polytypoid α-SiAlON (Sr 3 Si 24 Al 6 N 40 :Eu 2+ ) phosphor with three distinctive Sr/Eu luminescence sites using a solid-state remixing-reannealing process. The Sr content of this polytypoid structure exceeds those of a few previously reported structures by over 200%. The phase purity, composition, structure, and PL properties of this phosphor were investigated. A single phase can be obtained by firing the stoichiometric mixtures of all-nitride precursors at 2050°C under a 0.92 MPa N 2 atmosphere. The Sr 3 Si 24 Al 6 N 40 :Eu 2+ shows an intense orange-yellow emission, with the emission maximum of 590 nm and internal/external quantum efficiency of 66%/52% under 400 nm excitation. It also has a quite small thermal quenching, maintaining 93% emission intensity at 150°C. In comparison to Ca-α-SiAlON:Eu 2+ , this Sr counterpart shows superior quantum efficiency and thermal stability, enabling it to be an interesting orange-yellow down-conversion luminescent material for white LEDs. The experimental confirmation of the existence of such 'Sr-rich' SiAlON systems, in a single-phase powder form, paves the way for the design and synthesis of novel 'Sr-rich' SiAlON-based phosphor powders with unparalleled properties. A distinctive orange-yellow-emitting 'Sr-rich' α-SiAlON-based phosphor with quite small thermal quenching (93% PL intensity at 150°C) that can surprisingly be synthesized in a single-phase powder form for white LEDs.
materials science, multidisciplinary