Abstract:Controlling the interfacial interaction is a prerequisite for the preparation of aluminum matrix composites reinforced by carbon nanotubes (CNTs) with high performance. In this paper, Cu-coated CNTs fabricated by the compound reduction method were applied to control the interfacial interaction between carbon nanotubes and aluminum matrix for improving the interfacial bonding and mechanical properties of aluminum matrix composites. The microstructure, interfacial structure, interfacial interaction, and mechanical properties of Cu-coated composite were studied in detail. The in-depth study results show that Cu nanoparticles act as a bridge connecting the carbon nanotubes and matrix and forming Al2Cu intermetallic, which is in favour for better dispersion of carbon nanotubes and interfacial bonding. In addition, Cu nanoparticles are preferentially deposited at the defects of carbon nanotubes to repair the defects and inhibit the formation of brittle Al4C3 phases. As a result, Cu-coated composite displays the superior strength with yield strength and ultimate tensile strength of 203 MPa and 287 MPa, which are 45% and 38% higher than those of matrix (140 MPa and 207 MPa) and 8% and 12% higher than those of uncoated composite (188 MPa and 256 MPa), respectively. The introduction of Cu nanoparticles can significantly improve the interfacial bonding strength of Cu-coated composite, ensuring the effective transfer of load from the matrix to carbon nanotubes and exerting its strengthening and toughening effect.

Graphene-enhanced Cu Composite Interlayer for Contact Reaction Brazing Aluminum Alloy 6061

Preparation of the Graphene Nanosheets Reinforced AgCuTi Based Composite for Brazing Graphite and Cu

Three-dimensional Graphene-Reinforced Cu Foam Interlayer for Brazing C/C Composites and Nb

Study on Microstructures and Grain Boundary Penetration Behaviours in Contact Reactive Brazing Joints of 6063 Al Alloy

Contact Reactive Brazing of TC4 Alloy to Al7075 Alloy with Deposited Cu Interlayer

In-situ Alloying of BNi2+Ni Interlayer for Brazing C/C Composites and GH3536 Ni-based Superalloy

Chemically dealloyed Mg–Cu alloy lamina as an interlayer for reinforcing a C/C composite – TC4 alloy vacuum brazed joint

The Role of Active Cu Interlayer in Adjusting the Interfacial Reaction and Microstructure of Cf/C-DD3 Joints

Graphene-coated copper foam interlayer for brazing carbon/carbon composite and niobium

Brazing of SiC ceramic to Al<sub>0.3</sub>CoCrFeNi high entropy alloy by graphene nanoplates reinforced AgCuTi composite fillers

Effect of microelement on contact-reaction brazing of 6063 aluminum alloy

Brazing of C/C Composite and Ti-6Al-4V with Graphene Strengthened AgCuTi Filler: Effects of Graphene on Wettability, Microstructure and Mechanical Properties

Contact reactive brazing of Al7075 alloy using Cu layer deposited by magnetron sputtering

Study on the Residual Stress Relieving Mechanism of C/C Composite-Nb Brazed Joint by Employing a Structurally Optimized Graphene Reinforced Cu Foam Interlayer

Interface structure and mechanical performance of TLP bonded joints of Al2O3p/6061Al composites using Cu/Ni composite interlayers

Microstructural evolution of Ti–6Al–4V/UD-Cf/LAS composites joint brazed by graphene nanosheets reinforced composite filler

Β-Lialsio4 Reinforced Cu Composite Interlayer for Brazing C/C Composites and Nb

Effect of Cu interlayer with different thickness on microstructure and properties of Al2O3/Kovar joints brazed with Cu–Ti/Cu/BNi-2 composite filler

Interfacial Microstructure and Phase Constitution of the Cu/Al Dissimilar Metals Joint Made by Contact Reactive Brazing

Contact-reaction Brazing of an AZ31 Magnesium/3003 Aluminum Alloy Using a Silver-Copper-zinc Interlayer

Improvement of interfacial interaction and mechanical properties in aluminum matrix composites reinforced with Cu-coated carbon nanotubes