Abstract:The sericite mica was first treated by heating and acid dipping followed by LiNO3 treatment. The organophilic clay was subsequently achieved by inorganic-organic ion exchange in the hydrothermal reaction of LiNO3-treated sericite mica with intercalating agent-hexadecyltrimethylammonium bromide solution. Finally, a series of polyimide (PI)/sericite mica composites were prepared via in situ polymerization reaction. The effects of the reaction temperature and the amount of intercalating agent added on the modification of sericite mica were investigated. The structures of modified and original sericite mica were systemically characterized with Xray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM), showing the best intercalating effect was observed when the reaction temperature was 180 C and the amount of intercalating agent added was fifteenfold the cation exchange capacity (CEC). Under the above reaction conditions, the do basal spacing of the sericite mica was increased from 0.99 nm to 2.77 nm. The structure of the composites was investigated by XRD and high resolution transmission electron microscopy (HRTEM), and the thermal stability and the mechanical properties were studied by means of thermogravimetric analysis (TGA) and mechanical property measurements, indicating that the PI/original sericite mica composite was a simple physical blend of PI and pure sericite mica, while the PI/organic sericite mica nanocomposites was an exfoliated structure with 5 wt% loading and the nanocomposites with the content of 1 wt% 7 wt% organophilic sericite mica exhibited no observable peaks in the range of 0.5 degrees similar to 10 degrees (2 theta), which revealed that majority of the d(002)-spacing of organophilic sericite mica had been intercalated to a distance of more than 4.42 nm (2 theta < 1 degrees). When the mass ratio of sericite mica and PI was 5: 100, the tensile strength, Young's modulus and elongation at break of the PI/organic sericite mica nanocomposites are 1.79, 1.40 and 1.83 times those of the PI/original sericite mica counterpart, respectively. The thermogravimetric analysis showed that the thermal stability was tremendously enhanced with the increasing organophilic sericite mica content and the nanocomposites with 7 wt% loading revealed a 36 K increment in T-5 (the temperature at 5 wt% weight loss) compared with pristine PI.

Synthesis, Characterisation and Enhanced Properties of Polyimide/mica Hybrid Films

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

Polyimide/mica hybrid films with low coefficient of thermal expansion and low dielectric constant

Dielectric Properties of Polyimide‐Mica Hybrid Films

Preparation and Characterization of Polyimide/Alumina Composite Films As Improved Solid Dielectrics

Effects of various types of organo-mica on the physical properties of polyimide nanocomposites

Effect of Alumina on the Structure and Properties of Polyimide Matrix Films

Investigation of polyimide–mica hybrid films for cryogenic applications

The Fabrication and Properties of Polyimide/Silica-Alumina Hybrid Film

Research on the Synthesis and Properties of Polyimide/Montmorillonite Nanocomposite Film

Dielectric Properties of Polyimide/Mesoporous Silica Composite Films

Synthesis and Electrical Properties of Polyimide-Al2o3 Composites

Comparative Study on Morphology and Properties of Polyimide/silica Hybrid Films Derived from Different Polymeric Precursors

Preparation and Properties of Polyimides Based on Bis[3,5-Dimethyl-4-(4-Aminophenoxy)Phenyl]Methane

Preparation and properties of montmorillonite/organo-soluble polyimide hybrid materials prepared by a one-step approach

Synthesis and Characterization of Polyimide/Silica Nanocomposite Films

Preparation and characterization of polyimide/Al2O3 hybrid films by sol–gel process

Characteristics of electrical breakdown for MMT/PI hybrid films

Study of Preparation,Transparent Property and Thermal Insulation Property of Polyimide/SiO2 Hybrid Films

Preparation and Characterization of Polyimide/Sericite Mica Composites

Preparation, Microstructure, Mechanical, and Thermal Properties of in Situ Polymerized Polyimide/Organically Modified Sericite Mica Composites