Abstract:As semiconductor integration scales expand and chip sizes shrink, Through Silicon Via (TSV) technology advances towards smaller diameters and higher aspect ratios, posing significant challenges in thermo-mechanical reliability, particularly within interposer substrates where mismatched coefficients of thermal expansion exacerbate issues. This study conducts a thermo-mechanical analysis of TSV structures within multi-layered complex interposers, and analyzes the thermal stress behavior and reliability under variable temperature conditions (-55 °C to 85 °C), taking into account the typical electroplating defects within the copper pillars in TSVs. Initially, an overall model is established to determine the critical TSV locations. Sub-model analysis is then employed to investigate the stress and deformation of the most critical TSV, enabling the calculation of the temperature cycle life accordingly. Results indicate that the most critical TSV resides centrally within the model, exhibiting the highest equivalent stress. During the temperature cycling process, the maximum deformation experiences approximately periodic variations, while the maximum equivalent stress undergoes continuous accumulation and gradually diminishes. Its peak occurs at the contact interface corner between the TSV and Redistribution Layer (RDL). The estimated life of the critical point is 3.1708 × 105 cycles. Furthermore, it is observed that electroplating defect b alleviates thermal stress within TSVs during temperature cycling. This study provides insights into TSV thermal behavior and reliability, which are crucial for optimizing the design and manufacturing processes of advanced semiconductor packaging.

Effects of Post-Cmp Annealing on TSV Cu Protrusion and Leakage Current

Effect of Copper TSV Annealing on Via Protrusion for TSV Wafer Fabrication

Research on Effect of Annealing on Copper Deposited by Electroplating in High Density TSV

Influence of inhomogeneous anisotropic Copper grains in TSV on the thermo-mechanical behaviors in the annealing process

Electrothermal modelling of through silicon via (TSV) interconnects

Investigate the Microstructure Changes in Cu Through-Silicon Vias (tsvs) under Thermal Process

Modeling and Characterization of Annealing Effect on the Cu Protrusion and Thermomechanically Behaviors of Through Glass Via

Investigations of Annealing Effect on TSV CMP

Electrothermal modelling and characterisation of submicron through-silicon carbon nanotube bundle vias for three-dimensional ICs

Reliability Simulation Analysis of TSV Structure in Silicon Interposer under Temperature Cycling

Influence of annealing conditions on the mechanical and microstructural behavior of electroplated Cu-TSV

Optimization of Cu protrusion of wafer-to-wafer hybrid bonding for HBM packages application

Influence of Copper Pumping on Integrity and Stress of Through-Silicon Vias

Comprehensive study of the impact of TSV induced thermo-mechanical stress on 3D IC device performance

Reliability of Through-Silicon-vias (tsvs) with Benzocyclobutene Liners.

Impact of TSV Induced Thermo-Mechanical Stress on Semiconductor Device Performance

A Research Of The Micro-Damage Of The Backside Tsv Heterogeneous Microstructure After Cmp Process With Alkaline Slurry

The electromigration failure mechanism for TSV process

Thermal Reliability Tests of Air-Gap TSVs with Combined Air-SiO2Liners

Numerical and Experimental Investigation of Thermomechanical Deformation in High-Aspect-Ratio Electroplated Through-Silicon Vias

Thermal expansion coefficient of Cu-Al2O3 nanocomposites by molecular dynamics simulation