Study of Pre-stretching Fracture for Aluminum Alloy Thick Plates with Defects

DING Huafeng,ZHU Caichao,SONG Chaosheng

DOI: https://doi.org/10.3901/jme.2016.12.030

2016-01-01

Abstract:Due to the existence of defects, such as voids, in the material, the fracture of aluminum alloy thick plate will probably occur during the pre-stretching process, which is extremely harmful for the pre-stretching machine. The GTN damage constitutive is adopted to establish a model for pre-stretching fracture of aluminum alloy plate. The damage constitutive coefficients of GTN model are optimized by tensile fracture experiments and numerical simulations, five typical thicknesses of aluminum alloy plates are selected to investigate the pre-stretching fracture. The stress, strain and damage parameter of aluminum alloy plate during the fracture are calculated, the difference of variations on the surface and the fracture section are compared and discussed. The results show that, as the tension processing, the plane stress state in the aluminum alloy plate changes to strain concentration, and the location of concentration change from the center of the plate to edge position, meanwhile, the variations of the void volume fractions are the same as strain concentration; as the thickness of plate increasing, the fracture strain decreases slowly, and is affected by the void volume fraction significantly. Through the analysis of different thickness and tension ratio of pre-stretching aluminum alloy plates, the varying pattern of initial void volume fraction and the radii of initial voids with the thickness are obtained.