Energy-storage performance and pyroelectric energy harvesting effect of PNZST antiferroelectric thin films

Xiaolin Wang,Xihong Hao,Qiwei Zhang,Shengli An,Xiujian Chou
DOI: https://doi.org/10.1007/s10854-016-5679-7
2016-01-01
Abstract:In this work, (111)-oriented (Pb 0.99 Nb 0.02 )(Zr, Sn, Ti) 0.98 O 3 (PNZST) antiferroelectric thin films, which located in the tetragonal phase region (PNZST T ) and the orthorhombic phase region (PNZST O ), respectively, were successfully fabricated on platinum-buffered silicon substrates by radio-frequency magnetron sputtering technique. The microstructure, dielectric properties, electric field induced phase transition, associated with the energy-storage performance and pyroelectric energy harvesting behavior (by Olsen cycle) were studied systemically. The PNZST T thin film showed a diffused field-induced antiferroelectric–ferroelectric (AFE–FE) phase switching with a slim double hysteresis loop, while the PNZST O film demonstrated an AFE–FE phase switching with a square double hysteresis loop. A maximum recoverable energy-storage density of 16.4 and 12.4 J/cm 3 were obtained in the PNZST T and PNZST O film, respectively. Moreover, a huge harvested energy density per cycle of W = 7.35 and 5.35 J/cm 3 was also predicted in the PNZST T and PNZST O film at 1 kHz, respectively. The good energy-storage performance and giant thermal-electrical energy harvesting effect of the PNZST antiferroelectric thin films maybe make a great impact on the modern energy-storage technology and the thermal-electrical energy harvesting applications.
What problem does this paper attempt to address?