Enhanced Pyroelectric Properties and Application of Tetragonal Mn-doped 0.29Pb(in1/2nb1/2)o3-0.31Pb(mg1/3nb2/3)o3-0.40pbtio3 Ternary Single Crystals

Linrong Yang,Long Li,Xiangyong Zhao,Qing Xu,Jiashuai Ma,Sheng Wang,Xiaobing Li,Wenning Di,Haiqing Xu,Haosu Luo

DOI: https://doi.org/10.1016/j.jallcom.2016.07.314

IF: 6.2

2017-01-01

Journal of Alloys and Compounds

Abstract:Ferroelectric single crystals Mn-doped 0.29Pb(In1/2Nb1/2)O-3-0.31Pb(Mg1/3Nb2/3)O-3-0.40PbTiO(3) (Mn-PIMNT) have been grown by a modified Bridgman technique. The as-grown ternary tetragonal Mn-PIMNT (29/31/40) single crystals exhibit ultra-high Curie temperature T-C of 216 degrees C, 110 degrees C higher than that of Mn-PMNT(72/28) single crystals(T-d similar to 105 degrees C). In addition, the permittivity er of tetragonal Mn-PIMNT (29/31/40) is 350 at 1 kHz, approximately less than that of Mn-PMNT(72/28)(epsilon(r) similar to 640) in half. Moreover, as a core parameter of pyroelectric material, the figure of merits for detectivity (F-d) for Mn-PIMNT (29/31/40) is 23.5 x 10(-5)Pa(-1/2), close to that of Mn-PMNT(72/28)(Fd similar to 28.5). Finally, outstanding Mn-PIMNT(29/31/40) based pyroelectric detectors were fabricated, of which the specific detectivity (D*) (room temperature, 10 Hz) is up to 1.74 x 10(9) cmHz(1/2)/W for current-mode detectors, and 1.15 x 10(9) cmHz(1/2)/W for voltage-mode detectors, 3 times higher than that of commercial LiTaO3 based detectors. All of these results make these ternary tetragonal Mn-PIMNT single crystals a promising candidate for infrared detector applications. (C) 2016 Elsevier B.V. All rights reserved.