Abstract:One-step metal-assisted chemical etching (MACE) was used to fabricate porous silicon nanowire arrays. Also, the effects of doping level, AgNO3 concentration, and HF concentration on the morphology and structure of porous silicon nanowire were investigated. The results show that the higher doping level is beneficial for etching the silicon wafer and forming silicon nanowire arrays. This is because the higher doping level introduces more impurities and defects on the surface of the silicon wafer, and at the same time, the Schottky barrier between the silicon wafer with the higher doping level and the solution is lower. Thus, the silicon wafer is easier to oxidate to form nanowire arrays. The AgNO3 concentration plays a critical role in the fabrication of the porous silicon nanowire arrays during the one-step MACE process. If AgNO3 concentration is too low or too high, corrosion pits and collapsed clusters of nanowires could form on the surface of the silicon wafer. When AgNO3 concentration was 0.02 mol·L-1, silicon nanowires grew and became longer, eventually forming a porous array of silicon nanowire. In the meantime, as silicon nanowires grew, capillary stress between nanowires caused agglomeration at the top of some nanowires. Furthermore, when HF solution concentration exceeded 4.6 mol·L-1, the length of silicon nanowire increased with increasing HF concentration. Furthermore, a porous structure was formed on top the silicon nanowire, and the porosity of the silicon nanowires increased with increasing HF concentration. This was due to a large number of Ag+ random nucleations at the top of the nanowires, and lateral etching of the silicon nanowires occurred. In the end, the formation process of the porous silicon nanowires is explained by a model based on the experimental phenomena. It is attributed to the deposition of silver ions and the oxidation of dissolved silicon substrates.

Preparation of Porous Silicon Templates in Two Steps of Au-Assisted Chemical Etching

Porous Silicon Templates Prepared by Cu-Assisted Chemical Etching

Preparation of Large-Area Porous Silicon Through Cu-Assisted Chemical Etching

Optimization of Metal-Assisted Etchant Components for Fabrication of Porous Silicon

Facile Preparation of Porous Silicon from Silver-Assisted Chemical Etching Method on Silicon

Controllable and Facile Fabrication of Gold Nanostructures for Selective Metal-Assisted Etching of Silicon

Influence of Cu-assisted chemical etching preparation condition on the morphology of porous silicon

Study on Porous Silicon Template for Nanoimprint Lithography

Nanostructure Formation Via Print Diffusion Etching Through Block Copolymer Templates.

Preparation of Porous Silicon Microreactor Components Integrated with Microheater and Noble Metal Catalyst

Porous Silicon Nanowire Arrays Fabrication Through One-Step Metal-Assisted Chemical Etching

Metal-Assisted Chemical Etching Using Tollen’s Reagent to Deposit Silver Nanoparticle Catalysts for Fabrication of Quasi-ordered Silicon Micro/Nanostructures

A Template-Based Method for Preparing Ordered Porous Silicon

Preparation of Si Nanocrystals Using Anodic Porous Alumina Template Formed on Silicon Substrate

Fabrication of Silicon Nanopore Arrays with Three-Step Wet Etching

Controllable Fabrication of Silicon Nanopore Arrays by Two-Step Inductively Coupled Plasma Etching Using Self-Assembled Anodic Aluminum Oxide Mask

Preparation and Characterization of Porous Silicon in HF-AgNO3 Solution

Metal-assisted chemical etching of silicon: a review.

Fabrication Of Inverted-Pyramid Silicon Nanopore Arrays With Three-Step Wet Etching

Biological Functionalization and Patterning of Porous Silicon Prepared by Pt-assisted Chemical Etching

A novel method of fabricating porous silicon material: ultrasonically enhanced anodic electrochemical etching