Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

Facile Corrosion Synthesis and Sintering of Disperse Pure Tetragonal Zirconia Nanoparticles

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Mechanochemical dehydration and crystallization of supersaturated zirconia–alumina composite nano powders

Hydrothermal synthesis of (ZrO2)0.86(Sm 2O3)0.14 nano-powders and electrical properties of its sinter

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

From modification to mechanism: Supercritical hydrothermal synthesis of nano-zirconia

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Synthesis of the superfine high-entropy zirconate nanopowders by polymerized complex method

Ethanol-induced formation of precursor for 8mol% Yttria-stabilized zirconia: Towards the production of well-dispersed, easily sintering, and high-conductivity nano-powders