Abstract:Failure response of the modern high strength steel grades shows a diverse pattern compared to the conventional highly ductile steels. In automotive sheet forming applications of the high strength steels, fracture could be observed prior to necking or the post necking deformation is very limited. The differences in the underlying damage mechanisms contribute to the different ways of damage development and the interaction of damage with plastic localization and strain hardening creates various failure patterns. Therefore, it is critical to clearly identify the phase for damage initiation and understand the relation between plastic localization, damage and fracture, as these patterns significantly influence the safety assessment in the forming process of steels. Inverse modelling approaches are being used to bridge the gap between experiments and numerical simulations. However, this technique shows significant discrepancies when strain heterogeneity is experienced, especially since the determination of the material parameters is based on comparison on a global scale with force and elongation measurements. An iterative finite element model update (FEMU) procedure integrated with optical full field measurement technique was executed which extended the possibilities to identify the material ductile damage and fracture behavior on a local level with significantly higher accuracy. To identify the material plastic and damage behavior of the automotive dual phase steel (DP-K1000) under study, experiments are conducted on dog-bone, notched tensile, central hole and shear specimens at various strain rates. Full field deformation data was obtained by digital image correlation (DIC). A vigorous and general framework for the inverse identification of the strain hardening behavior up to fracture of the automotive high strength steel was studied. A hybrid damage mechanics model (extended Modified Bai-Wierzbicki) that combines a phenomenological criterion for damage initiation related to the microstructure degradation of materials and a continuum damage mechanics based damage evolution law for progressive damage accumulation till final fracture is employed using a VUMAT in the finite element (FE) scheme. To exclude the convergence (plastic instability) problems, a displacement driven finite element simulation was used while minimizing the discrepancy between the experimental and numerical surface strain fields and force values. A visual mapping procedure was adopted to realize identical reference frames and therefore identical peripheries for the specimen in DIC and FE model. This mapping includes a transformation and interpolation function from FE results to the DIC datum points. Successful identification of the material parameters was achieved based on a combined Gauss-Newton and Levenberg-Marquardt algorithm which require the evaluation of the gradient of the objective function to update the unknown parameters in an appropriate direction. The optimization problem of the inverse modelling in the current work was described by a cost function based on the least square norm of the differences of the surface strain fields. Overall cost function formulation is not dependent on the experimental or finite element meshes and includes rigid body motions. The residual was minimized at once for all the displacements by Gauss-Newton scheme in space-time, which is defined by spatial domain and temporal domain. The optimization of the constitutive parameters was directly achieved by minimizing this image residual in an iterative manner. The adopted methodology helped in determining macroscopic crack initiation instant and location from experiments. Local variables such as equivalent plastic strain, stress triaxiality and Lode angle parameter were evaluated from the critical element for the determination of the damage initiation locus which was then fitted by a non-linear least squares method with a trust-region algorithm in Matlab. The identified damage initiation locus and plastic localization phenomena served as an evaluation criteria for the formability of the dual phase automotive steel.

Numerical Prediction of the Formability During Hot Forming of High Strength Steel Based on Continuum Damage Mechanics

Enhanced CDM model accounting of stress triaxiality and Lode angle for ductile damage prediction in metal forming

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

Modeling the anisotropic plasticity and damage of AA7075 alloy in hot forming

Failure prediction of magnesium alloys based on improved CDM model

A Generalized Stress State and Temperature Dependent Damage Indicator Framework for Ductile Failure Prediction in Heat-Assisted Forming Operations

Revealing plastic localization and ductile damage initiation features with integrated DIC and FEM

Research on dynamic deformation behavior and constitutive relationship of hot forming high strength steel

A Multi-Phase Model for Transformation Plasticity Using Thermodynamics-Based Metallurgical Algorithm

Numerical Prediction and Experimental Investigation of Ductile Damage During Cold Upsetting of TC16 Titanium Alloy for Manufacturing Fasteners

Numerical prediction of ductile fracture in multi-stage single point incremental forming based on phenomenological modified Mohr–Coulomb

Formability prediction of high‐strength steel sheet using experimental, analytical and theoretical analysis based on strain and stress forming limit curves and its application to automotive forming parts

Forming Limit Prediction of Anisotropic Aluminum Magnesium Alloy Sheet AA5052-H32 Using Micromechanical Damage Model

A Physical-Based Plane Stress Constitutive Model for High Strength AA7075 under Hot Forming Conditions

Experimental and Numerical Determination of Hot Forming Limit Curve of Advanced High-Strength Steel

A rate-dependent damage mechanics model for predicting plasticity and ductile fracture behavior of sheet metals at high strain rates

A damage sequence interaction model for predicting the mechanical property of in-service aluminium alloy 6005A-T6

Calibration and application of damage and rate-dependent constitutive model for SPCE steel

Anisotropic ductile damage fully coupled with anisotropic plastic flow: Modeling, experimental validation, and application to metal forming simulation

Experimental and Numerical Investigation of Ductile Fracture of Carbon Steel Structural Components

Prediction of forming limit in the hydroforming processes by using FEM and fracture criterion