Abstract:A comparison study has been conducted on the formation of catalyst nanoparticles on a high surface tension metal and low surface tension oxide for carbon nanotube (CNT) growth via catalytic chemical vapor deposition (CCVD). Silicon dioxide (SiO2) and tantalum have been deposited as supporting layers before deposition of a thin layer of iron catalyst. Iron nanoparticles were formed after thermal annealing. It was found that densities, size distributions, and morphologies of iron nanoparticles were distinctly different on the two supporting layers. In particular, iron nanoparticles revealed a Volmer-Weber growth mode on SiO2 and a Stranski-Krastanov mode on tantalum. CCVD growth of CNTs was conducted on iron∕tantalum and iron∕SiO2. CNT growth on SiO2 exhibited a tip growth mode with a slow growth rate of less than 100nm∕min. In contrast, the growth on tantalum followed a base growth mode with a fast growth rate exceeding 1μm∕min. For comparison, plasma enhanced CVD was also employed for CNT growth on SiO2 and showed a base growth mode with a growth rate greater than 2μm∕min. The enhanced CNT growth rate on tantalum was attributed to the morphologies of iron nanoparticles in combination with the presence of an iron wetting layer. The CNT growth mode was affected by the adhesion between the catalyst and support as well as CVD process.

Influence of Catalyst Thickness on Diameters of Carbon Nanotubes

Influence of Catalyat Film Thickness on Carbon Nanotubes

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Effect of nickel catalyst thickness on growth of carbon nanotubes on glass nonwoven mat using thermal chemical vapor deposition method

Effects of Catalyst and Substrate on the Preparation of Carbon Nanotubes by ECR-CVD

The influences of synthesis temperature and Ni catalyst on the growth of carbon nanotubes by chemical vapor deposition

Effect of Nickel, Iron and Cobalt on Growth of Aligned Carbon Nanotubes

CVD Growth of Carbon Nanotube with Ni(OH)_2/SiO_2 Catalyst Synthesized by Hydrothermal Mthod:Influence of the Ni Content on the Diameter and Yield of Carbon Nanotube

Influence of Catalyst Film Thickness Deposited by Atomic Layer Deposition on the Growth of Aligned Carbon Nanotubes

The Effects of Catalyst Structure and Morphology on the Growth of Carbon Nanotubes

Effect of catalyst composition on carbon nanotube growth

Effects Of The Supporting Method Of The Active Constituent Of Catalyst On The Syntheses Of Carbon Nanotube Using Cvd Method

The effect of Fe and Ni catalysts on the growth of multiwalled carbon nanotubes using chemical vapor deposition

CVD growth of carbon nanotube with Ni(OH)2/SiO2 catalyst synthesized by hydrothermal method: Influence of the Ni content on the diameter and yield of carbon nanotube

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

Effect of catalyst on the growth of aligned carbon prepared by microwave chemical vapor deposition

Influence of Catalyst Structures on Carbon Nanotubes Growth Via Methane-CVD

Comparison study of catalyst nanoparticle formation and carbon nanotube growth: Support effect

Carbon Nanotube Growth on the Surface of Carbon Fibers by CVD