Abstract:To improve the wear resistance of high chromium white cast iron under severe abrasive conditions, a composites layer was designed for wear surface, which were locally reinforced with WC particles. And the local composites were successfully fabricated by optimized centrifugal casting process. Then the interface between WC and iron matrix was analyzed with scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD). And three body wear tests were carried out on a self-made rig to investigate the wear resistance of the composites. For comparison, the wear tests of high chromium white cast iron were also carried out under the same conditions. The results show that: There are no defects such as inclusion, crack, gas pore and so on in the obtained composites layer, which with a uniform thickness of 10 mm. WC particles are homogeneously distributed in the composites layer and tightly bonded with the iron matrix. The WC particles are partially dissolved in the iron matrix during centrifugal casting. The elements W, C and Fe react to form new carbides such as Fe3W3C or M23C6, which precipitate around former WC particles during subsequent solidification. So the interface between WC particles and the iron matrix is a strong metallurgical bonding. WC particles in the composites layer can effectively resist cutting by the abrasive, and then protect the matrix. The wear resistance of the composites layer is 7.23 times of that of high chromium cast iron.

Search for New Materials for Slurry Pumps with Erosion-wear Resistance

Research on WC/Cast Iron Matrix Surface-layer Composites for Slurry Pumps

Study on the erosion wear characteristics and mechanisms of UBHMWPE/kaolin composites

Study of New Material with Erosive-Wear Resistant Used in Hydraulic Power Stations in Slurry Water

Selection of Surface-Layer Composites for the Parts of Slurry Pump

Study on Erosive Wear and Novel Wear-Resistant Materials for Centrifugal Slurry Pumps

Interfacial Characteristics and Wear Resistance of WCp/White-Cast-Iron Composites

Interfacial characteristics and wear resistance of WCp/white-cast-ion composites

Erosive Wear Resistance of Particle Reinforced Stainless Steel Composites

Study of Abrasive Wear Resistant of WC Particle Reinforced Chromium White Cast Irons Matrix Composite

Abrasive Erosion Comparison for A Ceramics and A High Chrome Cast Iron Applied in A Slurry Pump

Study on Surface WC Particle Reinforced Chromium Abrasion Resistant White Cast Irons Composite

Investigates of Three-body Abrasive Wear Behavior of WC Particles Reinforced Chromium Family White Cast Irons Composites

Solid Particle Erosion of WC Particles Reinforced Steel matrix Composites

Interfacial characterization and erosive wear performance of zirconia toughened alumina ceramics particles reinforced high chromium white cast irons composites

Microstructure and Wear Behavior of High-Cr WCI Matrix Surface Composite Reinforced with Cemented Carbide Rods

Production and Properties of Local Strong Anti-Abrasive Composite

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

Elucidation of Abrasive Wear and Slurry Erosion Behavior of Fe Matrix Composites Reinforced with Metallic Coating Modified ZTAP Ceramics

Investigation of Erosion Properties of Particle Reinforced Epoxy Wear Resistant Coating

Interaction Between Erosive-Wear and Corrosion of Alloy Materials for Hydroturbine in Hydroelectric Station