THE MICRO-STRUCTURE OF CARBON-COATED IRON PARTICLES AND RADIALLY-GROWN CARBON NANOTUBES

沈曾民,刘云芳,传秀云,于建民
DOI: https://doi.org/10.3969/j.issn.1001-3741.2003.02.002
2003-01-01
Abstract:Using benzene and toluene as carbon source, ferrocene as catalyst with a kind of sulphur compound as promoter, carbon-coated-iron particles and radially-grown carbon nanotubes were prepared by the catalytic pyrolysis method,and the effect of the flow rate of H2 on the growth of the products was studied. The morphology and structure of the carbon-coated particles and carbon nanotubes were examined by TEM and HRTEM, and the growth mechanism of these nanomaterials was discussed. The results show that under the same conditions (carbon source, catalyst and temperature), two types of carbon nanotubes, straight and non-straight, are synthesized with the flow rate of H2 being 5 400 mL/min. The inner diameter of the straight nanotubes is larger than that of the non-straight ones. When the flow rate of H2 is 2 000 mL/min, about 90% of the products are the carbon-coated iron particles with an average size of about 530 nm. Other products are some radially-grown carbon nanotubes with outer diameter of 45-50 nm and inner diameter of 3-5 nm.
What problem does this paper attempt to address?