Abstract:Simultaneously achieving high-quality catalytic cracking of light tar, maintaining a large target product yield and improving the reductivity of iron ore, is major step towards enhancing the energy conversion efficiency of the coal chemical industry and ironmaking applications. To achieve the aforementioned goals, an experiment involving regulation under coal pyrolysis, with iron ore as a catalytic bed, optimization of carbon deposition in spent samples and integration of multiple similar reaction factors between the pyrolysis of experimental samples and volatile decomposition-carbon deposition was designed. The mass fraction and yield of the light tar produced when the pyrolysis tar is passed through a goethite bed are 75.1 % and 5.34 % at the upper reactor temperature of 550 degrees C, respectively, which are higher than those of the other two iron ore. Additionally, because the iron ore contains carbon deposits at the nanometre scale, compared with the original iron ore, the spent sample exhibits a peculiar phenomenon in which the reactivity increases. The reduction degree, metallization ratio of the iron ore and kinetic characteristics are compared and analysed, confirming a response mechanism to enhance the reduction degree on various fluctuating factors at temperatures exceeding 800 degrees C, and revealing that the reduction reaction occurs consecutively in four consecutive according to the efficiency of the conversion. In absence of sufficient CO2 in the reaction and according to the calculated activation energy, the carbon gasification reaction was identified as a rate-limiting step in the reduction reaction. The activation energy and rate-limiting step provide a pathway featuring pollution reduction, clean energy and energy conservation aimed towards the deployment of integrated technology for tar upgrading and iron ore reduction.

The Activity Regeneration of Deactivate Calcium Oxide With Coking

Investigation of the deactivaty of a kind of circulating ash when the tar cracking over it

Advances in calcium carbonate thermal decomposition

INVESTIGATION OF CATALYTIC DEACTIVITY AND ACTIVITY REGENERATION OF CIRCULATING ASH OF CFBB IN TAR CRACKING REACTIONS

Deactivation and Burning Regeneration of Coked Acid Catalysts in Catalytic Cracking Process of Biomass Tar

Study On The Deactivation And Activity Regeneration Of Catalyst In Biomass Tar Cracking

Regeneration of Deactivated Circulating Ash Using Coking in a CFBB

Effect of Cracking Reactions of Tar Components on Activity of CFBB Circulating Ash

Experimental Investigation on Catalyst Deactivation in Catalytic Cracking of Biomass Tar

Catalytic cracking reactions of tar components over CaO

Catalytic Cracking and Catalyst Deactivation/regeneration Characteristics of Fe-loaded Biochar Catalysts for Tar Model Compound

Catalytic Effect of Alkali Metals on the Gasification Dissolution Reaction and Deep Reaction Behavior of Metallurgical Cokes.

Experimental investigation on catalytic cracking reactions of main components of tar over circulating ash of CFBB

The Rate-Limiting Step in the Integrated Coal Tar Decomposition and Upgrading-Iron Ore Reduction Reaction Determined by Kinetic Analysis

Deactivation Mechanism of CeO2-Based Mixed Oxide Catalysts Supported on SiO2

Mechanism of In-Situ Catalytic Cracking of Biomass Tar over Biochar with Multiple Active Sites

Influence of Catalytic Cracking of Tar on Gas Component

Coking and Regeneration of Nickel Catalyst for the Cracking of Toluene As a Tar Model Compound

Experimental Study on Catalytic and Thermal Cracking of Tar from Biomass Pyrolysis

Effects of Catalytic Cracking Conditions on Biomass Tar Cracking

Effects of Solid Acid and Alkali Catalysts on Catalytic Cracking of Biomass Tar