Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

PREPARATION OF HYDROPHOBIC SiO2 AEROGEL AT LOWER COST

Study on Silica Aerogel Modified by Trimethylchlorosilane

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Preparation of Low Density Hydrophobic Silica Aerogels by Controlling Strength of Alcogels

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Preparation and Characterization of Hydrophobic Silica Aerogel by Ambient Pressure Drying Method

Preparation of Hydrophobic Silica Aerogels from Industrial Water Glass

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Synthesis and characterization of low density and hydrophobic silica aerogels dried at ambient pressure using sodium silicate precursor

Rapid synthesis of sodium silicate based hydrophobic silica aerogel granules with large surface area

Synthesis of Hydrophobic Silica Aerogels via Ambient Pressure Drying

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Convenient and rapid preparation of aerogels dried at ambient pressure

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique

A Facile Strategy for Freeze-Drying Preparation of Silica Aerogel from Sodium Silicate

Preparation and properties of hydrophobic and highly transparent SiO 2 aerogels

Preparation of superhydrophobic and flexible polysiloxane aerogel

Influence of Hydrolysis Time on Properties of SiO2 Aerogels Prepared by Ambient Pressure Drying

Superhydrophobic silica aerogel powders with simultaneous surface modification, solvent exchange and sodium ion removal from hydrogels

Preparation of high-strength silica aerogels by two-step surface modification via ambient pressure drying

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent