Abstract:Ultrafine copper powders were prepared by the air-jet milling of copper oxide (CuO) powders and a subsequent hydrogen (H2) reduction. After milling, the particle size and grain size of CuO powders decreased, while the specific surface area and structural microstrain increased, thereby improving the reaction activity. In a pure H2 atmosphere, the process of CuO reduction was conducted in one step, and followed a pseudo-first-order kinetics model. The smaller CuO powders after milling exhibited higher reduction rates and lower activation energies compared with those without milling. Based on the unreacted shrinking core model, the reduction of CuO powders via H2 was controlled by the interface reaction at the early stage, whereas the latter was limited by the diffusion of H2 through the solid product layer. Additionally, the scanning electron microscopy (SEM) indicated that copper powders after H2 reduction presented a spherical-like shape, and the sintering and agglomeration between particles occurred after 300 °C, which led to a moderate increase in particle size. The preparing parameters (at 400 °C for 180 min) were preferred to obtain ultrafine copper powders with an average particle size in the range of 5.43–6.72 μm and an oxygen content of less than 0.2 wt.%.

Advance on Study of Cu Nano-powders

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics

Study on Preparation and Application of Nano-copper Powder for Power Semiconductor Device Packaging

Hydrothermal Preparation of CuAlO2 Powder

Preparation of Ultrafine Cu 2 O Powders with Different Morphologies from Cu(OH) 2 Gel

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Preparation of CuO-TiO2 nanocrystalline powders by the sol-gel method

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

Preparation and Characterization of Talc/Nano-Cu Conductive Composite Powder

Preparation and optical properties of Cu2O hollow microsphere film and hollow nanosphere powder via a simple liquid reduction approach

Preparation of ultrafine copper powders by NH2NH2 center dot H2O-HCHO direct reduction method and glucose prereruction method

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Preparation of copper nano-particle by homogeneous reduction method

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

One-Pot Fast Synthesis of Leaf-Like CuO Nanostructures and CuO/Ag Microspheres with Photocatalytic Application

Preparation of Copper Nanoparticles with Low Sintering Temperature

Preparation and Particle Size Characterization of Cu Nanoparticles Prepared by Anodic Arc Plasma