Preparation Process and Resin Properties Control of the Toner in Suspension Polymerization

何虹,杨俊,王亭杰,金涌

DOI: https://doi.org/10.3321/j.issn:1003-9015.2001.06.006

2001-01-01

Abstract:Toner preparation process and the resin composition control in suspension polymerization were researched for improving the application properties of the toner. Bulk polymerization process of styrene was studied in the presence of carbon black, iron black pigments and ultrasonic action, respectively. Experimental results showed that the ultrasonic effect on the bulk polymerization of styrene can be divided into three stages. In the earlier stage, the polymerization was accelerated due to the remarkable effect of ultrasonic polymerization. In the middle stage, the polymerization was retarded due to the decomposition effect of ultrasonic on polymerized resin. In the later stage, the ultrasonic polymerization was accelerated remarkably again due to the high viscosity of reactant slurry. Non-reactive surface of the iron black particles speeded polymerization for its hindering termination of chain radicals, and with the increase of adding amount of iron black, the accelerating function was more remarkable. Adding low amount of carbon black accelerated the polymerization, while adding large amount resulted in hindering the polymerization of styrene. Because the resin characteristics in toner affect the fixation quality crucially in printing process, the effect of reaction temperature, the amount of initiator and pigments of carbon black and iron black on the average molecular weight and its distribution, softening point and melt index were studied in this research. The average molecular weight and the polydispersity (ratio of weight average molecular weight to number average), softening point and melt index were employed as characterization parameters. Research results showed that increasing the reaction temperature or the initiator amount, the resin molecular weight decreases, the softening point decreases and the melt index increases. Adding carbon black results in the decrease of molecular weight, which results from that the active functional groups on the surface of carbon black can trap the chain radical. Adding iron black retards coupling termination, and polymer resin with higher molecular weight and wider distribution forms, which leads to that the softening point increases and the melt index decreases. Therefore, the resin properties can be controlled through the adjustment of parameters in the suspension polymerization process.