Abstract:It is well known that magnetic nanofluids are widely applied in various fields ranging from heat transfer to miniature cooling, and from damping to sealing, due to the mobility and magnetism under magnetic field. Herein, the PFPE-oil based magnetic nanofluids with superior magnetization and dispersion stability were obtained via regulating reaction temperature. The structures of particles were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The size effects of particles on the magnetism and coating effect of particles, and on the stability and saturation magnetization of the fluids were characterized by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), vibrating sample magnetometer (VSM) and density instrument, respectively. The results indicate that the impurity phase FeOOH only appear in the sample prepared at 18°C and the average size of Fe 3 O 4 nanoparticles reduces from 120 to 20 nm with raising reaction temperature. The saturation magnetization of Fe 3 O 4 particles increases firstly and then reduces with increasing particle size, which is affected by the thickness of magnetic dead layer and impurity phase FeOOH. The Fe 3 O 4 particles could be chemically coated by PFPE-acids, and the coated mass is a little affected by particle size. The stability of the nanofluids lowers while the saturation magnetization increases firstly and then decrease with increasing particle size. At reaction temperature of 60°C, Fe 3 O 4 particles of 25 nm and the nanofluids with superior stability and saturation magnetization were obtained. Our results indicate that the control of nanoparticles size by regulating reaction temperature can be a useful strategy for preparing magnetic nanofluids with desirable properties for various potential applications.

The Size Distribution Characteristics of Magnetic Particles Prepared by Suspension Polymerization

Micron-Size Functional Uniform Pmma Particles by Dispersion Copolymerization in Polar Media

Studies on the magnetic polymer material of polyolefin with nanometer magnetic dispersing phase. (2) The measurement of particle size and particle size distribution of nanometer ultrafine particles

Mechanism and Model of Dispersion Polymerization Using Homopolymer As Dispersant in Polar Media

Particle Size Distribution And Morphology Of Suspension Polymerized Mono-Component Magnetic Toner

Preparation and Colloidal Stability of Monodisperse Magnetic Polymer Particles

Particle Size Distribution And Morphology Of In Situ Suspension Polymerized Toner

STUDY ON THE FORMATION MECHANISM OF MONODISPERSE PARTICLES IN THE EMULSIFIER-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Polymer Modification of Ultrafine Metal Iron Particles and Magnetorheological Properties of Their Suspensions

Particle size control and the interactions between drug and stabilizers in an amorphous nanosuspension system

Preparation of Magnetic Polymeric Particles Via Inverse Microemulsion Polymerization Process

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Formation of Monodispersed Polymer Particles in Emulsifier-Free Emulsion Polymerization

Formation Mechanism of the Monodispersed Particles in the Emulsifier-Free Emulsion Polymerization ---- System of Methyl Methacrylate / Butyl Acrylate

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

In Situ Dispersion of Non-Aqueous Fe3O4 Nanocolloids by Microdroplet Coalescence and Their Use in the Preparation of Magnetic Composite Particles.

Preparation of magnetic polymer nanosphere and its profile control

Size Effect of Fe3O4 Nanoparticles on Magnetism and Dispersion Stability of Magnetic Nanofluid

Particle Size Dependent Rheological Property in Magnetic Fluid

Preparation and Characterization of Micron‐sized Magnetic Microspheres by One‐step Suspension Polymerization

Influence of synthesis conditions on the structure and size of magnetite nanoparticles in co-precipitation method without stabilizer in one system