Abstract:The mechanism of the film-coating process of hydrated alumina on TiO2 particles in aqueous solution was experimentally studied. pH and zeta-potential changes during the mixing process of the TiO2 suspension and Al-2(SO4)(3) solution were investigated. TiO2 particles obviously promote the hydrolysis of Al-2(SO4)(3) in both acidic and basic solutions and adsorb positively charged OH-Al species in slurries. A static repulsion dominates the suspension system of OH-Al species and TiO2 particles, in which they randomly collide with each other because they carry the same sign of charge. When the OH-Al species or TiO2 particles have enough energy to cross the repulsion threshold, the -OH groups on the surface of the TiO2 particles will condense with the OH-Al species, leading to the coating of OH-Al species on the surface of the TiO2 particles. However, completely inelastic collisions also occur between the OH-Al species, and the formation of hydrous alumina is unavoidable unless the local concentration of the coating reagent in the suspension is well controlled. The morphology and surface chemical states of coated TiO2 particles were also analyzed by high-resolution transmission electron microscopy (HRTEM) and X-ray photoelectron spectroscopy (XPS). TiO2 particles coated with hydrous alumina exhibit electrokinectic behavior similar to that of pure Al(OH)(3) gel.

Preparation of Al2O3-coated TiH2 Foaming Reagent by Chemical Method

Preparation and Releasing Hydrogen Characteristic of Al2O3-Coated TiH2 Particles

Preparation of TiO2‐Coated Al2O3 Particles by Chemical Vapor Deposition in a Rotary Reactor

The effect of SiO2 and Al2O3 coating on the surface of TiH2 powders on gas release.

Development of AlMg35-TiH2 composite foaming agent and fabrication of small pore size aluminium foams

Preparation of Titanium Coating on Alumina Foam by Chemical Vapor Deposition

Titania Polyhedra Via Sodium Fluorotitanate Intermediates

Preparation of NiAl2O4/Al2O3 composite nanopowder

Hydrothermal Preparation of CuAlO2 Powder

Effect of SiO2 coating layer morphology on TiH2 gas release characteristic.

Influences Of Agglomeration Powder Preparation On Deposition Of Cold-Sprayed Ti2alc Coating

Formation of Al2O3–TiO2 Composite Oxide Films on Aluminum Foil by Cathodic Electrodeposition and Anodizing

Film-Coating Process of Hydrated Alumina on TiO<sub>2</sub>Particles

The coating process of silica film on TiH2 particles and gas release characteristic

Photocatalytic activities of TiO2 and TiO2/Al2O3 films coated on foam nickel substrates

Preparation of TiO2 Powders with Different Morphologies by an Oxidation-Hydrothermal Combination Method

Coating process of silica film on TiH2 particles and hydrogen release characteristics

Process study of TiO2 coating on Al2O3 particles by chemical vapor deposition technology

Formation of Na3AlH6 from a NaH/Al Mixture and Ti-containing Catalyst

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Differences among SiO2, TiO2, and Ti in the anti-foaming mechanism of chemically bonded silicate coatings