Abstract:The internal void defects often exist in the large ingot inevitably due to the non-uniform solidification of the materials. To guarantee the mechanical performance of the products, these voids should be closed and eliminated in the subsequent forging process. The main purpose of this study is to investigate the void closure efficiency in different cogging processes of large ingot by using a 3-D void evolution model. In order to obtain a more reasonable description of the actual engineering condition, the voids were considered as prolate ellipsoidal, and the influences of the instantaneous void shape changing, stress state and deformation history were taken into account for the void evolution. According to the results, alternate compression in different directions makes the changing of the void shape counteracted and decreases the void closure efficiency. The initial void shape impacts the void closure significantly, as the non-spherical void shape causes the anisotropy of the void closing behavior. It can be found that the compression perpendicular to the longer principal axis of the prolate void provides the higher void closure efficiency than the compression aligned with this direction. Therefore, using the extend-forging as the first step in cogging process is more efficient to close the voids, considering the morphology of the real voids in the ingot. Moreover, appropriate processing parameters were determined to enhance the void closure efficiency in extend-forging. Besides, the surface bonding experiments show that the high pressure and temperature, as well as the long holding time, are favorable to eliminate the void defects after the void closure. It implies that the processing sequence, which can make the void closed completely at high pressure and high temperature and keep the sufficient interval time between forming stages, should be emphasized in the process planning.

A STUDY OF LOCAL EFFECTS OF PORE AND CRITICAL REDUCTION FOR PORE CLOSURE IN HEAVY INGOTS

A Study of Critical Reduction for Closing Pores in Heavy Forgings

Void Closing Conditions for Solid Cylinders During Hot Forging

Simulation of cylindrical up setting of porous materials by finite element method

A criterion for void closure in large ingots during hot forging

Modeling and Numerical Simulation Research on Hollow Steel Ingot Forging Process of Heavy Cylinder Forging

A Porosity Closure Model for the Integrated Casting and Forging Process of Aluminum Alloy and Its Application

Z-C Criterion of Void Closure for Large-ingot Hot Forging and Its Application

Numerical simulation of casting-forging integrated breakdown process

Analysis of Internal Cracks in High Carbon Casting Bloom Induced by Soft Reduction Process and Its Improvement Using Numerical Simulations and Industrial Experiments

Investigation on the Void Closure Efficiency in Cogging Processes of the Large Ingot by Using A 3-D Void Evolution Model

Influence of process conditions and pore morphology on the closure rate of pores in hot rolling of steel

Numerical Simulation of Pore Evolution of 7050 Aluminum Alloy during Hot Compression Process

Study of workability limits of porous materials under different upsetting conditions by compressible rigid plastic finite element method

Investigation on hollow steel ingot forging process of heavy cylinder forging

Shrinkage Porosity Model for Steel Ingots with Reduction Deformation during Solidification

Computer Modeling of Property-controlled Forging Process for Heavy Forgings

Numerical simulation of shrinkage porosity defect in billet continuous casting

Study on the Bonding Condition of Inner Crack Defects in Heavy Forgings

Microstructure Refinement and Crack Initiation in the Forging Process

Research on Heavy Hollow Ingot Forging Process