Abstract:The most common defect found in the high pressure die casting(HPDC) process is gas porosity which significantly affects the mechanical properties of the final components.As it is known,the air entrapment of the liquid metal flow during the mold filling stage has a close relationship with the gas porosity distribution in die castings.The generation of the entrapped air is mainly due to the interaction between air and liquid metal in the die cavity.In the past few decades,extensive efforts have been made to develop numerical models for the simulation of mold filling.However,these efforts mainly focused on the single phase flow models which can only predict the liquid metal flow and assume that the effect of air in the die cavity is negligible.As a result, these models could not provide the quantity and location of entrapped air in die castings.Recently, several research results on tracking the entrapped air in the molten metal flow have been reported but some techniques still need to be improved further and much more researches are required.In this study,a liquid-gas coupled model is presented to simulate the air entrapment phenomenon during the HPDC mold filling process.The pressure of the entrapped air bubbles is solved at each time step. The calculations of the liquid and gas phases are combined together through the pressure transfer.In order to verify the validity and stability of this model,a specially designed water analog experiment was carried out and compared with the numerical simulation results of the liquid-gas coupled model and the single phase flow model,respectively.The comparison shows that the liquid-gas coupled model has better prediction accuracy than the single phase flow model in tracking the entrapped air bubbles.

Study on the Critical Mould Entry Velocities of Thin-wall Castings by Numerical Simulation

Revealing the Relationship Between Critical Inlet Velocity and a Double-Layer Oxide Film Combined with Low-Pressure Casting Technology

Research on Casting Process for Embedded Internal Flow Passage Mould

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Research Progress on Modeling and Simulation of Air and Oxide Film Entrapment During Mold Filling of Aluminum Casting

Study on numerical simulation of mold-filling and solidification processes of shaped casting

Modeling Coupled Fluid Flow and Heat Transfer During the Low Pressure Casting Process of Thin-Walled Plate Castings

The molding analysis of automobile parts using the die-casting system

Effect of Depressurizing Speed on Mold Filling Behavior and Entrainment of Oxide Film in Vacuum Suction Casting of A356 Alloy

Numerical Simulation of Air Entrapment Phenomenon During Mold Filling of High Pressure Die Casting Process

Dynamic Model of Mold Filling Process under Low Pressure Casting

Numerical simulation and experimental verification of the initial temperature distribution of castings during mold filling process

Numerical Simulation of Mold Filling During Centrifugal Casting of TiAl Alloy Exhaust Valve

Numerical simulation and optimization of liquid metal flow in the shot sleeve of cold chamber die casting process

Study and Application of Mold Filling Simulation of Shaped Castings

Mold filling velocity during investment casting

Numerical Simulation of the Flow Field in an Ultrahigh-Speed Continuous Casting Billet Mold

Study on the Influence of Injection Velocity on the Evolution of Hole Defects in Die-Cast Aluminum Alloy

Study on Numerical Simulation of Mold Filling and Heat Transfer in Die Casting Process

Numerical Study on Characteristic Positions and Transition of Flow Patterns in a Slab Continuous Casting Mold

183/1 Research on mould filling process of melt in vertical centrifugal casting