Abstract:Photocatalysis-assisted chemical mechanical polishing, in which the photocatalysis oxidation and silica abrasives polishing are combined, is a novel finishing technique for 4H–SiC wafer. This paper characterizes the effect of pressure and abrasives on the MRR and surface quality and discusses mechanical and chemical interaction based three slurries that resulted in maximum material removal rate (1.18 μm/h) with PCMP slurry. The polished silicon carbide wafer was examined with atomic force microscope, transmission electron microscope and X-ray photoelectron spectroscopy for surface quality and material removal mechanism. The results show that an atomically smooth and flat 4H–SiC (0001) surface (Ra about 0.247 nm) was obtained by PCMP. The interface of crystal and amorphous layer of 4H–SiC wafer was flat without introducing crystallographic subsurface damage, and the atoms and lattice fringes of the crystal layer are arranged in regular order. The existence of a thin silicon oxycarbide layer, which are various forms of functional groups such as Si–C, Si–C–O, Si–O, Si4C4O4, C–O, and C = O, at the interface. And, it also demonstrates that the amorphous layer is composed of oxide layer (4–6 nm) and distorted layer. The silicon carbide surface is mechanically activated, oxidized and mechanically removed in turn, which is the main method of material removal.

Chemical mechanical planarization of silicon wafers at natural pH for green manufacturing

Chemical effect on the material removal rate in the CMP of silicon wafers

Research on the Chemical Mechanical Polishing Process of Aluminum Alloy Wafers with Acidic Slurry

Chemical mechanical polishing of silicon wafers using developed uniformly dispersed colloidal silica in slurry

Enhancing Slurry Stability and Surface Flatness of Silicon Wafers through Organic Amine-Catalyzed Synthesis Silica Sol

Optimization of polishing fluid composition for single crystal silicon carbide by ultrasonic assisted chemical-mechanical polishing

Accelerated C-face polishing of silicon carbide by alkaline polishing slurries with Fe3O4 catalysts

Material Removal Mechanism of Copper CMP from a Chemical–Mechanical Synergy Perspective

Achieving Ultralow Surface Roughness and High Material Removal Rate in Fused Silica Via a Novel Acid SiO2 Slurry and Its Chemical-Mechanical Polishing Mechanism

Effect of pH on Material Removal Rate of Cu in Abrasive-Free Polishing

Single crystal silicon wafer polishing by pretreating pad adsorbing SiO2 grains and abrasive-free slurries

Investigation on Material Removal Mechanisms in Photocatalysis-Assisted Chemical Mechanical Polishing of 4H–SiC Wafers

XPS, UV–vis Spectroscopy and AFM Studies on Removal Mechanisms of Si-face SiC Wafer Chemical Mechanical Polishing (CMP)

Chemical Mechanical Polishing of Mo Using H2O2 as Oxidizer in Colloidal Silica Based Slurries

Improvement in chemical mechanical polishing of 4H-SiC wafer by activating persulfate through the synergistic effect of UV and TiO2

Chemical mechanical polishing for sapphire wafers using a developed slurry

Chemical Mechanical Polishing of Aluminum Alloys using Alumina-Based Slurry

Chemical Mechanical Planarization (cmp) of On-Axis Si-Face Sic Wafer Using Catalyst Nanoparticles in Slurry

Angstrom surface with high material removal rate for quartz glass induced by silk dissolved novel green chemical mechanical polishing

Effect and Mechanism of Dual-Official Group of Ethanolamines on the Chemical Mechanical Polishing of Monocrystalline Silicon

Chemical-mechanical synergies effects of multi-purpose pH regulators on C-, A-, and R-plane sapphire polishing