Abstract:Irradiation assisted stress corrosion cracking (IASCC) of austenitic stainless steel core components is one major concern for maintenance of nuclear power plants. Previous studies on the IASCC had mainly focused on the effect of irradiation on changes in deformation modes and interaction of dislocation channels with grain boundary. The role of corrosion in IASCC, however, has not received sufficient attentions. In the process of stress corrosion cracking (SCC), corrosion occurs simultaneously with localized deformation in the vicinity of the crack tip. This indicates that corrosion is one of the potential contributors to IASCC. In this work, IASCC of proton-irradiated nuclear grade 304 stainless steel (304SS) was investigated. The IASCC tests were conducted by interrupted slow strain rate tensile (SSRT) tests at 320 degrees C in simulated primary water of pressurized water reactor containing 1200 mg/L B as H3BO3 and 2.3 mg/L Li as LiOH center dot H2O, with a dissolved hydrogen concentration of 2.6 mg/L. Following the SSRT tests, the localized deformation, corrosion and IASCC of the specimens were characterized. The results revealed that increasing the irradiation dose promoted residual strain accumulation at slip steps and grain boundaries of nuclear grade 304SS. Since the slip step usually transmitted or terminated at the grain boundary, it eventually promoted localized deformation at the grain boundary. Specially, the slip step transmitted at grain boundary led to slip continuity at the grain boundary. In contrast, a slip discontinuity was observed at the grain boundary where the slip step terminated, which caused a much higher strain accumulation by feeding dislocations to the grain boundary region. Further, formation of the slip discontinuity was related to the Schmidt factor pair type of the adjacent grains. The irradiation resulted in a depletion of Cr and an enrichment of Ni at grain boundary, while the magnitude of Cr depletion and Ni enrichment increased with increasing the irradiation dose. Following the SSRT tests, intergranular cracking was observed on surfaces of the irradiated specimens, while the number of the cracks was increased by a higher irradiation dose and applied strain. This suggested a higher IASCC susceptibility of nuclear grade 304SS in the primary water. Meanwhile, significant intergranular oxidation ahead of the crack tip was observed, while both the width and length of the oxide were larger at a higher irradiation dose. The synergic effect of irradiation-promoted deformation and intergranular corrosion was the primary cause for the IASCC of the irradiated steel.

Review of Irradiation Assisted Stress Corrosion Cracking of Core Structural Materials

How irradiation promotes intergranular stress corrosion crack initiation

Study on Irradiation Assisted Stress Corrosion Cracking of Nuclear Grade 304 Stainless Steel

Review of Stress Corrosion Cracking of Structural Materials in Nuclear Power Plants

A micromechanical analysis of intergranular stress corrosion cracking of an irradiated austenitic stainless steel

A high-resolution characterization of irradiation-assisted stress corrosion cracking of proton-irradiated 316L stainless steel in simulated pressurized water reactor primary water

A Review of Corrosion Failure of Welded Structural Metallic Materials for Light Water Reactor Plant

Decoupling the roles of grain boundary oxidation and stress in IASCC of neutron-irradiated 304L stainless steel

Theoretical models for irradiation hardening and embrittlement in nuclear structural materials: a review and perspective

Understanding Stress Corrosion Cracking (SCC), Affecting Variables and Prevention Strategies in Nuclear Power Plants—A Review

Proton Irradiation Assisted Localized Corrosion and Stress Corrosion Cracking in 304 Nuclear Grade Stainless Steel in Simulated Primary PWR Water

Deformation and Cracking Behaviors of Proton-Irradiated 308L Stainless Steel Weld Metal Strained in Simulated PWR Primary Water

Chloride-induced stress corrosion cracking in Austenitic steels for SNF storage canisters - Recent understanding and advances in mitigation and repair

Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment

Radiation Effects in Novel Nuclear Materials

The Effect of Post-Irradiation Annealing on the Stress Corrosion Crack Growth Rate of Neutron-Irradiated 304L Stainless Steel in Boiling Water Reactor Environment

Study of Irradiation Damage in Domestically Fabricated Nuclear Grade Stainless Steel

Review on SCC Crack Growth Behavior of Dissimilar Metal Welds for Nuclear Power Reactors

Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment

Review on Core Degradation and Material Migration Research in Light-Water Reactors

Intergranular stress distributions in polycrystalline aggregates of irradiated stainless steel