Abstract:Low alloy SA508 bainitic steel is often welded to 300 series austenitic stainless steel in nuclear power plants. These dissimilar metal weldments use 309L butter applied to the low alloy steel and 308L groove filler material to join the 309L to austenite. High alloy steels (such as the 308L and 309L material used here) have been identified as having greater susceptibility to irradiation-assisted stress corrosion cracking (IASCC). Evidence is presented here of cracking under tensile loads in 309L weldment butter in LWR hydrothermal conditions that correlates irradiation induced changes at δ ferrite−γ austenite phase boundaries and γ−γ grain boundaries; specifically intergranular Cr 23 C 6 precipitates. Cracking is not observed in irradiated 308L groove filler under the same conditions. Both the 309L butter and 308L filler material have a duplex or mixed δ−γ phase microstructure due to solidification during the welding procedure. We have performed constant extension rate autoclave immersion tests in BWR normal water chemistry hot water (288 °C, 10 MPa, 2000 wt. ppb dissolved oxygen, <100 nS/cm conductivity, neutral pH) of proton irradiated (2 MeV, approximately 3 displacements per atom at a depth of 10 μm). Proton irradiation to the dpa levels used here induced Cr 23 C 6 carbide precipitation at γ−γ grain boundaries and δ−γ phase boundaries in the 309L butter but not the 308L filler. Cracking was observed in the proton-irradiated volume of 309L at these interfaces in the vicinity of the Cr 23 C 6 precipitates. We hypothesis the SA508 is the source of carbon in the 309L butter. Cr depletion at γ−γ grain boundaries was also observed and may also be a root cause of cracking. The 309L butter is under significant tensile residual stress in the weldment that adds to applied tensile loads and this too may be a contributing factor.

Proton Irradiation Assisted Localized Corrosion and Stress Corrosion Cracking in 304 Nuclear Grade Stainless Steel in Simulated Primary PWR Water

A high-resolution characterization of irradiation-assisted stress corrosion cracking of proton-irradiated 316L stainless steel in simulated pressurized water reactor primary water

Irradiation Assisted Stress Corrosion Cracking of 347 Stainless Steel in Simulated PWR Primary Water containing Lithium Hydroxide or Potassium Hydroxide

Crack initiation of neutron-irradiated 304 L stainless steel in PWR primary water

The time dependence of proton irradiation effect on the intergranular oxidation of 316L stainless steel in high-temperature hydrogenated water

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Unveiling the synergistic effect of thermal aging and irradiation corrosion on the passivation performance and stress corrosion cracking of 308 L stainless steel under high-temperature water environment

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

A micromechanical analysis of intergranular stress corrosion cracking of an irradiated austenitic stainless steel

Effect of heavy ion irradiation on the electrochemical behavior of 321 stainless steel

Decoupling the roles of grain boundary oxidation and stress in IASCC of neutron-irradiated 304L stainless steel

Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment

Clarifying the mitigation effect of proton irradiation on the intergranular oxidation of 316L stainless steel in high temperature water

IASCC of neutron irradiated 316 stainless steel to 125 dpa

Clarifying the irradiation effect on the general oxidation of 316L stainless steel in high temperature hydrogenated water after 1000 h immersion

In-situ proton irradiation/lead-bismuth eutectic corrosion synergistic effect on corrosion behaviour of 11Cr1W1Si ferritic/martensitic steel

Corrosion behaviour of nanocrystallines 304 stainless steel in simulated secondary side environment

Irradiation damage and corrosion performance of proton irradiated 304 L stainless steel fabricated by laser-powder bed fusion

Effects of Dissolved Gas and Cold Work on the Electrochemical Behaviors of 304 Stainless Steel in Simulated PWR Primary Water

How irradiation promotes intergranular stress corrosion crack initiation

Mechanistic understanding of the localized corrosion behavior of laser powder bed fused 316L stainless steel in pressurized water reactor primary water