Abstract:In this work, amorphous thin films in Mg-Si-O-N system typically containing >15 at.% Mg and 35 at.% N were prepared in order to investigate especially the dependence of optical and mechanical properties on Mg composition. Reactive RF magnetron co-sputtering from magnesium and silicon targets were used for the deposition of Mg-Si-O-N thin films. Films were deposited on float glass, silica wafers and sapphire substrates in an Ar, N2 and O2 gas mixture. X-ray photoelectron spectroscopy, atomic force microscopy, scanning electron microscopy, spectroscopic ellipsometry, and nanoindentation were employed to characterize the composition, surface morphology, and properties of the films. The films consist of N and Mg contents up to 40 at.% and 28 at.%, respectively and have good adhesion to substrates and are chemically inert. The thickness and roughness of the films increased with increasing content of Mg. Both hardness (16–21 GPa) and reduced elastic modulus (120–176 GPa) are strongly correlated with the amount of Mg content. The refractive index up to 2.01 and extinction coefficient up to 0.18 were found to increase with Mg content. The optical band gap (3.1–4.3) decreases with increasing the Mg content. Thin film deposited at substrate temperature of 100 °C shows a lower value of hardness (10 GPa), refractive index (1.75), and higher values of reduced elastic modulus (124 GPa) as compared to the thin film deposited at 310 °C and 510 °C respectively, under identical synthesis parameters.

Investigation on A Magnesiothermic Reduction Process for Preparation of Nanocrystalline Silicon Thin Film

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

A study of sputtering process for nanocrystalline FeAlN soft magnetic thin films

Unlocking the Secrets of Porous Silicon Formation: Insights into Magnesiothermic Reduction Mechanism using In-situ Powder X-ray Diffraction Studies

Preparation of Mesoporous Si Nanoparticles by Magnesiothermic Reduction for the Enhanced Reactivity

Preparation of silicon crystallites via controllable thermal reduction of amorphous silica

Microstructure and Conductivity of Large Area Nanocrystalline Silicon Films Grown by Specially Designed Thermal-Assisted Chemical Vapor Deposition

A Study on the Heat Effect during Magnesiothermic Reduction of Porous SiO2

Preparation and Photoluminescence of Nanocrystalline Si-Rich Silicon Oxide Films by Pecvd

The effect of stoichiometric ratio of Mg/SiO2 and annealing on physical properties of silicon nanoparticles by magnesium-thermic chemical reduction process using the SiO2 precursor

Formation of silicon layer through aluminothermic reduction of quartz substrates

Investigation on the Magnetic and Electrical Properties of Crystalline Mn0.05si0.95 Films

In Situ Formation of Nanoporous Silicon on a Silicon Wafer via the Magnesiothermic Reduction Reaction (MRR) of Diatomaceous Earth

Preparation of Porous Silicon by Magnesiothermic Reduction from Serpentine

Mg2Si Promoted Magnesio-Mechanical Reduction of Silica into Silicon Nanoparticles for High-Performance Li-ion Batteries

Investigation of Mn-doped Si films prepared by magnetron cosputtering

Optical and mechanical properties of amorphous Mg-Si-O-N thin films deposited by reactive magnetron sputtering

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Characterization of Sn and Si nanocrystals embedded in SiO2 matrix fabricated by magnetron co-sputtering

Nanoscale structural characterization of manganite thin films integrated to silicon correlated with their magnetic and electric properties