Grain refinement and strengthening of additively manufactured Nb by doping TiC nanoparticle prepared via laser directed energy deposition

Da Liu,Wei Liu,Yuanyuheng Wang,Youxing Yu,Jiangbo Sha,D. Liu,W. Liu,Y.Y.H. Wang,Y.X. Yu,J.B. Sha

DOI: https://doi.org/10.1016/j.addma.2024.104129

IF: 11

2024-04-11

Additive Manufacturing

Abstract:Additive manufacturing is a promising net-shape production methodology; however, coarse columnar grain structures and undesirable defects (such as cracking and porosity) may remain in the products. In this work, we demonstrate a valid strategy that is introduction of TiC nano-powders to restrict directional grain growth for controlling microstructures with crack-free and near-equiaxed grains in alloys composed of Nb x TiC (where TiC is a nanoparticle and x = 0, 1, 2 and 3 wt.%) using laser directed energy deposition (L-DED) technology. The dependence of the microstructural evolution, tensile properties, and deformation behavior of the Nb x TiC alloys on the L-DED process parameters and the TiC contents were investigated. The optimal parameters of 800 W and 800 mm/min resulted in a near-equiaxed grains along the building direction, without hot cracks and pores. Rod-like or needle-like α-Nb 2 C carbides were formed in situ along the Nb grain boundaries and within Nb grains, and TiC nanoparticles were uniformly distributed within the Nb grains. The 0.2% yield strength (σ 0.2 ), ultimate tensile strength (σ b ) and plastic elongation (ε f ) of the L-DED Nb/TiC ingots significantly increased as the TiC content increased from 0% to 3 wt%. The high-density pile-ups of tangled dislocations formed around the carbide, and the abundantly movable dislocations and kinks within the Nb grains, played key roles in the strengthening and toughening mechanisms of the L-DED Nb x TiC alloys, respectively.

engineering, manufacturing,materials science, multidisciplinary