Abstract:Using Fe-MgO, Co-MgO and Ni-MgO catalysts preparated by citric acid method, carbon nanotubes (CNTs) were synthesized from decomposition of methane at 873 K, 973 K and 1013 K, respectively, and were characterized by TEM and Raman spectra. The effects of catalysts, preparation temperature and reaction time on the shape, yield and inter - structure of carbon nanotubes were discussed.TEM results and Raman spectra show that the shapes and inter-structures of carbon nanotubes produced on different catalysts at the same temperature are quite different. Carbon nanotubes synthesized on Fe-MgO incline to be rods, with very thick wall, and the diameter varied greatly from 10 nm to 80 nm. However, the diameter of carbon nanotubes produced on Co-MgO is about 35 nm, and about 20 nm on Ni-MgO. As can see from the Raman spectra, the G peaks of carbon nanotubes produced on the three catalysts shift slightly, which indicate the difference of the inter-structure of nanotubes.The experiments show that the yield of carbon nanotubes varied with decomposition temperature. Using Fe-MgO catalysts, yield of carbon nanotubes grows with the decomposition temperature. However, using Ni-MgO catalysts, the yield drops when the temperature increases. The reaction temperature with the largest yield of carbon nanotubes is higher than 1013 K on Fe-MgO catalysts, about 973 K on Co-MgO catalysts, and lower than 873 K on Ni-MgO catalysts, respectively.The results also show that the yield of carbon nanotubes does not increase with the decomposition time. There is a saturation time of the carbon nanotube growth. The carbon nanotubes do not grow any more when the saturation time reaches. For example, on Ni-MgO catalysts, the carbon nanotubes stop growing after decomposition of CH4 for 2 h.

Large-Scale Preparation of Carbon Nanotubes Via Catalytic Pyrolysis of Phenolic Resin at Low Temperature

Preparation and Growth Mechanism of Carbon Nanotubes Via Catalytic Pyrolysis of Phenol Resin

Facile synthesis of carbon nanotubes via low temperature pyrolysis of ferrocene

Production of Carbon Nanotubes with Different Shapes by Catalytic Pyrolysis of Methane

Preparation of Well-Aligned Carbon Nanotubes by Pyrolysis of Phenolic Resin in Anodic Alumina Pores

Identify the impact of pyrolysis temperature on preparation of carbon nanotubes by catalytic reforming polypropylene

Pyrolytic Synthesis of Conical Carbon Fibers with Carbon Nanotube Tips on Carbon Substrates

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

Nanostructured Hybrid Carbon Nanotube/UltraHigh‐Temperature Ceramic Heterostructures: Microstructure Evolution and Forming Mechanism

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Preparation and Purification of Carbon Nanotubes by Catalytic Decomposition

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

The Factors of Preparation of Carbon Nanotubes by Catalytic Decomposition of Methane

Mechanism of carbon nanotube growth in expanded graphite via catalytic pyrolysis reaction using carbores P as a carbon source

Synthesis and Characterization of Larger Diameter Carbon Nanotubes from Catalytic Pyrolysis of Polypropylene

A one-step single source route to carbon nanotubes

Carbon nanotube prepared by catalytic pyrolysis of methane

Homogeneous carbon nanotube/carbon composites prepared by catalyzed carbonization approach at low temperature

Carbon Nanotube Synthesis from Alcohol Using Catalytic Pyrolysis Method