Abstract:Using Fe-MgO, Co-MgO and Ni-MgO catalysts preparated by citric acid method, carbon nanotubes (CNTs) were synthesized from decomposition of methane at 873 K, 973 K and 1013 K, respectively, and were characterized by TEM and Raman spectra. The effects of catalysts, preparation temperature and reaction time on the shape, yield and inter - structure of carbon nanotubes were discussed.TEM results and Raman spectra show that the shapes and inter-structures of carbon nanotubes produced on different catalysts at the same temperature are quite different. Carbon nanotubes synthesized on Fe-MgO incline to be rods, with very thick wall, and the diameter varied greatly from 10 nm to 80 nm. However, the diameter of carbon nanotubes produced on Co-MgO is about 35 nm, and about 20 nm on Ni-MgO. As can see from the Raman spectra, the G peaks of carbon nanotubes produced on the three catalysts shift slightly, which indicate the difference of the inter-structure of nanotubes.The experiments show that the yield of carbon nanotubes varied with decomposition temperature. Using Fe-MgO catalysts, yield of carbon nanotubes grows with the decomposition temperature. However, using Ni-MgO catalysts, the yield drops when the temperature increases. The reaction temperature with the largest yield of carbon nanotubes is higher than 1013 K on Fe-MgO catalysts, about 973 K on Co-MgO catalysts, and lower than 873 K on Ni-MgO catalysts, respectively.The results also show that the yield of carbon nanotubes does not increase with the decomposition time. There is a saturation time of the carbon nanotube growth. The carbon nanotubes do not grow any more when the saturation time reaches. For example, on Ni-MgO catalysts, the carbon nanotubes stop growing after decomposition of CH4 for 2 h.

Carbon nanotube prepared by catalytic pyrolysis of methane

Production of Carbon Nanotubes with Different Shapes by Catalytic Pyrolysis of Methane

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

The Factors of Preparation of Carbon Nanotubes by Catalytic Decomposition of Methane

Growth of Carbon Nanotubes by Catalytic Decomposition of CH4 or CO on a NiMgO Catalyst

Pyrolytic Synthesis of Carbon Nanotubes on Ni, Co/MCM-41 Catalysts

Preparation and Growth Mechanism of Carbon Nanotubes Via Catalytic Pyrolysis of Phenol Resin

Preparation of Carbon Nanotube by Reacting Ch4 over Ni-Based Catalysts

Intrinsic Kinetics of Pyrolysis of CH4 to Grow CNTs over a Ni-Mg-O Catalyst

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Mass Production of High-Quality Multi-Walled Carbon Nanotube Bundles on a Ni/Mo/MgO Catalyst

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

Carbon nanotubes production from catalytic pyrolysis of polyethylene over nickel-based catalysts: The influence of support materials

Synthesis of Carbon Nanotubes by Catalytic Chemical Vapor Deposition over Methane Reduced Ni Catalyst

Production of Carbon Nanotubes with Marine Manganese Nodule As a Versatile Catalyst

Preparation and Purification of Carbon Nanotubes by Catalytic Decomposition

Synthesis Of Close-Packed Multi-Walled Carbon Nanotube Bundles Using Mo As Catalyst

Study on Carbon Nanotubes of Pyrolysis Carbons P for In Situ Catalytic Formation on Expanded Graphite Surface

Mechanism of carbon nanotube growth in expanded graphite via catalytic pyrolysis reaction using carbores P as a carbon source

Catalytic Vapor Decomposition of Methane over Nickle Catalyst: Growth Rate and the Corresponding Microstructures of Carbon Nanofibers