Abstract:The present work investigated the influences of the variation of Si content and the minor amount of Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys systematically. Alloy compositions with Nb-21.6(Ti/Zr)-3.1Hf-(9.4–15.6)Si-6.3Cr-3.1Al-1.0B (at. %) were designed using a cluster formula approach to realize the substitution of similar elements, in which these alloys were solid-solutionized at 1573 K for 24 h and then aged at 1273 K for 24 h. It was found that all these aged alloys are mainly composed of BCC-Nb solid solution (Nbss), Nb 5 Si 3 and Cr 2 Nb phases, where the increase of Si content and the addition of Zr could significantly increase the volume fraction of Nb 5 Si 3 in a form of coarse and primary particles. Consequently, high-Si alloys possess outstanding mechanical property at high temperature, as evidenced by the fact that the yield strength ( σ YS = 373 MPa) at 1523 K of high-Si/Zr alloy containing 15.6 at. % Si and 1.6 at. % Zr is much higher than that ( σ YS = 266 MPa) of the low-Si alloy with 9.4 at. % Si and 0 Zr. It is mainly ascribed to the existence of primary Nb 5 Si 3 particles, besides the eutectic microstructure composed of Nbss and Nb 5 Si 3 , as well as fine Cr 2 Nb precipitates in Nbss. Moreover, a minor amount of Zr substitution for the Ti is conducive to the phase transition of α-Nb 5 Si 3 to γ-Nb 5 Si 3 . Thus, this high-Si/Zr alloy exhibits an improved oxidation resistance after 50 h-exposure at 1523 K, due to the lowest mass gain of about 80.9 mg/cm 2 . The constitutions of oxide scales in these alloys were characterized and compared, from which it was found that the better oxidation resistance is closely related to the formation of dense oxide scales. This work will provide a new approach to obtain an optimum combination of mechanical property and oxidation resistance of superalloys through multi-component alloying.

High-temperature Oxidation Behavior of Nb–Si-based Alloy with Separate Vanadium, Tantalum, Tungsten and Zirconium Addition

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

High-throughput experiment-assisted study of the alloying effects on oxidation of Nb-based alloys

High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Improving oxidation resistance of TaMoZrTiAl refractory high entropy alloys via Nb and Si alloying

Effects of Si variation and Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys

High-Temperature Oxidation of NbTi-Bearing Refractory Medium- and High-Entropy Alloys

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Microstructure and Oxidation Behavior of Nb-Si-Based Alloys for Ultrahigh Temperature Applications: A Comprehensive Review

High Temperature X-Ray Diffraction Study of the Effect of Nb and Si on Oxidation Behavior of Ti3Al Alloy

Oxidation behavior of Nb-16Si-20Ti-3Al containing nano-ZrC fabricated by laser melting deposition

Oxidation behavior of Ti-Nb-Mo-Al-Six refractory high entropy alloy at 1000°C

Microstructure and oxidation behavior of Nb-based multi-phase alloys

On the Microstructure and Properties of Nb-18Si-6Mo-5Al-5Cr-2.5W-1Hf Nb-Silicide Based Alloys with Ge, Sn and Ti Additions (at.%)

Cyclic oxidation behavior of Nb/Mn/Si alloying beta-gamma TiAl alloys

The Mechanical Properties and High-Temperature Oxidation Behavior of (Tizr)65-X-ynb15mo20sixaly Refractory High Entropy Alloys

The high-temperature oxidation behavior and mechanism in a powder metallurgy Ni-based superalloy featuring δ-Nb3Al addition

The Mechanical Properties and High-Temperature Oxidation Behavior of (Tizr)65-X-ynb15mo20sixaly 65-X-y Nb 15 Mo 20 Si X Al Y Refractory High Entropy Alloys

Early oxidation behavior of Ti50Al and Ti45Al8Nb alloys

Effects of Al/Si on the oxidation behavior of a TiZrV0.5Nb0.5 refractory high entropy alloy at 1000 °C