Abstract:The wetting behaviors of α‐Al2O3 single crystals with three different faces—R(0112), A(01120), and C(0001)—and polycrystals (PC) by molten aluminum were studied over a wide temperature range using both a conventional and an improved sessile‐drop method. The critical factors affecting the wettability, such as temperature, atmosphere, substrate surface roughness, and crystallographic orientation, and the influence from the experimental technique, were thoroughly investigated. The results show that the aluminum surface oxidation and the thickness of the oxide film have a pronounced effect on the wettability, especially at low temperatures. To eliminate this effect, the experimental temperature must be over a critical value. Vacuum favors lowering this value compared with atmosphere, and the improved sessile‐drop method, particularly using an impingement‐dropping mode (I‐mode), helps to weaken this effect by mechanical disruption and removal of the oxide film. However, the dropping distance and the dropping force must be controlled to prevent an overspreading of the drop. The effects of the substrate surface roughness and temperature are not significant in the case of a clean aluminum surface and a fine‐prepared alumina surface. On the other hand, the effect of the alumina surface crystallographic orientation is noticeable and the wettability is in the order of R > A > PC > C. The intrinsic contact angles of the Al/α‐Al2O3 system in the temperature range of 1000°–1500°C were estimated to be 76°–85° for the R and A faces, 88°–100° for the C face, and 77°–90° for the polycrystal, depending on the temperature.

Influence of AlN(0001) Surface Reconstructions on the Wettability of an Al/AlN System: A First-Principle Study

Adsorption and Reaction of Water on the AlN(0001) Surface from First Principles

Surface Preparation and Homoepitaxial Deposition of AlN on (0001)-Oriented AlN Substrates by Metalorganic Chemical Vapor Deposition

Influence Of Alpha-Al2o3 (0001) Surface Reconstruction On Wettability Of Al/Al2o3 Interface: A First-Principle Study

Influence of interfacial configuration on bonding strength and wettability between CuNiTi active filler metal and AlN ceramic

Computational Study on Carbide and Nitride Treatments of W-Aln(0001) Substrate

First-principles calculations of the effects of the interface microstructure on the wettability of a Cu–Ti/AlN system

Wurtzite AlN(0001) Surface Oxidation: Hints from Ab Initio Calculations

Influence of AlN Ceramic Substrate Surface Treatment on Thin Film Adhesion

Critical Factors Affecting the Wettability of Α‐alumina by Molten Aluminum

Molecular dynamics and first-principles calculations on the wetting behavior and mechanism of molten Al on nickel-infiltrated steel: A cross-scale simulation

Influence of AlN Ceramic Surface State on Adhesion of Ti/Ni Metallized Thin Films

The Wettability and Interfacial Characterization Between Γ-Tial Alloy and Ceramic Reinforcements

Surface Orientation and Wetting Phenomena in Si/α‐Alumina System at 1723 K

Decorating nano Ni on the surface of CNTs and their wettability behaviors analysis with aluminum alloy

Reconstruction and Stability of AlxGa1-xN (0001) and (000) Surfaces with Different Al Compositions: A Density Functional Study

Effect of Al Substrate Nitridation on the Properties of AlN Films Grown by Pulsed Laser Deposition and Its Mechanism

Effects of aluminum diffusion on the adhesive behavior of the Ni(1 1 1)/Cr2O3(0 0 0 1) interface: First principle study

Understanding the surface adsorption and oxidation of cubic Cr0.5Al0.5N by first-principles calculations

Wettability of TiAlN films by molten aluminum

Influence of Nickle Coated on Alumina Nano-powder on Wetting Behavior of Alumina Ceramics with Aluminum