Abstract:The as-cast and annealed Fe 76 Si 19.4 Nb 2.7 Cu 1.7 P 0.2 ribbons with width of 2.5 cm prepared by a single-roller cooling method were investigated. The structural properties of ribbons were studied by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). The XRD result shows the α-Fe crystal phase of annealed film. The average crystallite sizes of the as-cast and annealed ribbons are about 28 nm and 43 nm obtained from EF-SEM. The dielectric and magnetic properties of ribbons were tested over frequency ranges of 5 MHz to 300 MHz and 5 MHz to 3000 MHz using an Impedance Analyzer, respectively. The dielectric constant and dielectric loss of the as-cast ribbon decreases from 4.3 × 10 5 to 180 and from 3.01 to 0.06, while that of annealed ribbon decreases from 2.5 × 10 4 to 180 and from 3.01 to 1.31. The permeability decreased with increasing frequency at first of each ribbon and the value of annealed ribbon is bigger. It was observed that the permeability loss value of annealed ribbon is smaller at first and then bigger than that of as-cast ribbon. The smallest values of permeability of the as-cast and annealed ribbons are about 1.4 and 1.8. The minimum of the permeability loss of the as-cast ribbon is 0.008. The magnetic hysteresis loops were investigated using a vibrating sample magnetometer. The saturation magnetizations of the as-cast and annealed ribbons are 113 emu g −1 and 123 emu g −1 . The coercive fields of the as-cast and annealed ribbons are 259 A m −1 and 1130 A m −1 . The saturation magnetization and coercive field could become bigger due to the crystallize property.

The effect of ribbon curvature on the magnetic properties of Fe-based amorphous cores

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Effect of CO gas on surface profile and magnetic properties of Fe–Si–B amorphous ribbons

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Study of dielectric and magnetic properties with Fe76Si19.4Nb2.7Cu1.7P0.2 ribbons

Revealing the effects of cooling rate on soft magnetic properties of (Fe0·9Co0·1)86Ni1B13 amorphous alloy

Soft magnetic properties and giant magneto-impedance effect of Co68.15Fe4.35Si12.5B15-Cr amorphous ribbons

Magnetic and Magneto-Caloric Properties of the Amorphous Fe92−xZr8Bx Ribbons

Magnetic and Magneto-Caloric Properties of the Amorphous Fe<sub>92-x</sub>Zr<sub>8</sub>B<sub>x</sub> Ribbons

Influence of Magneto-Thermal Treatments on Longitudinally Driven Giant Magneto-Impedance Effect in Co-Fe-Si-B Amorphous Ribbons

Reducing the Core Losses of Fe-Si-B Amorphous Alloy Ribbons by High Cooling Rate Planar Flow Casting

Effect of low-temperature transverse field annealing on domain structure and soft magnetism of Fe53-xCo7Ni20Si4B16Crx (x = 0, 1, 2, 3) amorphous alloys

Properties and analysis of coercivity mechanism of NdFeB nanocrystalline magnetic alloys

Analysis of the coercivity of amorphous ferromagnetic alloys

Magnetic properties of CoFeSiBMo amorphous ribbons for MI element application

Influence of Corrosion on the Magnetic Properties of Amorphous and Nanocrystalline FeZrNbBCu Alloy

Comparative study on the structure and magnetic properties of Sm10Co60Fe15(Al, B)15 amorphous-nanocrystalline ribbons

Off-diagonal magnetoimpedance in field-annealed Co-based amorphous ribbons

Effects of Ribbon Thickness on Structure and Soft Magnetic Properties of a High-Cu-Content FeBCuNb Nanocrystalline Alloy