Fabrication and properties of a high porosity h-BN–SiO2 ceramics fabricated by stereolithography-based 3D printing
Zhuo Tian,Yuping Yang,Yong Wang,Haidong Wu,Wei Liu,Shanghua Wu
DOI: https://doi.org/10.1016/j.matlet.2018.10.058
IF: 3
2019-02-01
Materials Letters
Abstract:In this paper, BN–SiO2 porous ceramics with high porosity have been successfully fabricated using bottom-up digital light processing (DLP) stereolithography and pressureless sintering. The phase composition, microstructure, compressive strength, dielectric properties and porosity of the porous material were investigated. The results show that the skeleton of the porous material was composed of h-BN, and the silica was ‘coated’ on the surface of the h-BN particles. The dielectric constant, dielectric loss, compressive strength and porosity of the material were 1.41–1.45, 1.85 × 10−3–1.93 × 10−3, 11.2 MPa, 77.2%, respectively. These characteristics make the h-BN–SiO2 porous ceramics useful in wave-transmitting field.