Study on thermal conductivity of expanded graphite/copper composites enhanced by TiC

Pu-jie Sun,Hong-da Du,Wei Chen,Yuan-yuan Zhang,Jia Li,Jin-zao Xu,Lin Gan,Fei-yu Kang

DOI: https://doi.org/10.14078/j.cnki.1001-3741.2017.05.005

2017-01-01

Abstract:The edges of graphite nanoplatelets of compressed expanded graphite (CEG) are modified with TiC, which was synthe-sized by reacting TiCl4 directly with CEG at high temperatures. The composites of edge-modified CEG-TiC and copper were pre-pared by liquid impregnation and hot press process. The experiments were conducted to study the effects of TiC on the thermal con-ductivity of CEG, as well as the thermal conductivities of CEG-TiC/Cu composites. The experimental results indicate that TiC on CEG can effectively improve the thermal paths to increase the thermal conductivity of CEG. The thermal conductivity of the CEG-TiC and copper composites increases first, and then decreases, with the increase of TiC. The increase of thermal conductivity at small amount of TiC is because, that the chemical compatibility between TiC and copper is better than the compatibility between CEG and copper. On the other hand, an excess of TiC may form a TiC layer with very low conductivity, leading to the decrease of the thermal conductivity of composites. In summary, it is conceived that the proper amount of TiC can effectively improve the thermal conductiv-ity of the expanded graphite and improve the interfacial compatibility of the CEG and copper, thus increasing the thermal conductiv-ity of the composites.