Abstract:TiC bonded diamond composites were prepared from a mixture of Ti, graphite, and diamond powders as raw materials, with Si as sintering additives, through high-temperature and high-pressure (HTHP) technology. The reaction between Ti and graphite under 4.5–5 GPa pressure and 1.7–2.3 kW output power can produce TiC as the main phase. The diamond particles are surrounded by TiC, and the interface is firmly bonded. The coefficient of friction (COF) of TiC–diamond composites with POM and PP balls decreases with increasing load for a specific friction velocity. However, the COF of TiC–diamond composites with agate, Cu and Al balls increases with the rising load because of the enhanced adhesive wear effect. The COF of PP, Cu and Al balls slightly increases with the increase in friction velocity at a certain load. SEM results show that the surface of agate balls has rough, pear-shaped grooves and shallow scratches. The scratches on the surface of POM balls are wrinkled. The PP balls have pear-shaped groove scratches on their wear surfaces. The wear mechanism of TiC–diamond composites with Cu ball pairs is primarily adhesive wear. The abrasion of TiC–diamond composites with Cu ball pairs remains almost unchanged as the load increases. However, the depth and width of the pear-shaped grooves on the wear surface of TiC–diamond composites are significantly increased. This phenomenon may be attributed to the high rotational speed, which helps to remove the residual abrasive debris from the friction grooves. As a result, there is a decrease in both the depth and width of the pear-shaped grooves, leading to a smoother overall surface. The wear mechanism of TiC–diamond composites with Al ball pairs is abrasive wear, which increases with an increasing load. When the load is constant, as the speed increases, the wear morphology of TiC–diamond composites with Al ball pairs transitions from rough to smooth and then back to rough again. This phenomenon may be attributed to the wear mechanism at low speeds being groove wear and adhesive wear. As the speed increases, the wear particles are more easily removed from the wear track, leading to a reduction in abrasiveness. As the speed increases, the wear surface becomes roughened by a combination of grooves and dispersed wear debris. This can be attributed to the increased dynamic interaction between surfaces caused by higher speed, resulting in a combination of abrasive and adhesive wear. In addition, Cu and Al ball wear debris appeared as irregular particles that permeated and adhered to the surface of the TiC phase among the diamond particles. The results suggest that TiC–diamond composites are a very promising friction material.

Synergistic optimization of mechanical and tribological properties of TiC modified copper-graphite composites by direct current in-situ sintering

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Enhanced mechanical and tribological properties of copper matrix composites reinforced by copper-coated graphite and Ti3AlC2

Effect of Ti3SiC2 replacing graphite on the microstructure and properties of Cu-Sn matrix composites

Synergetic influence of TiCnp and graphite particles on tribological performance of Cu based composites prepared by flake powder metallurgy

Optimization of the mechanical properties of CNTs/Cu composite by regulating the size of interfacial TiC

Tribological synergy of copper‐based metal–organic frameworks, carbon fibers and SiO2 in modifying the friction and wear properties of epoxy composites

Effect of sintering temperature on microstructure and tribological properties of copper/graphite composites doped with Ti3AlC2 particles

Microstructure and tribological properties of titanium matrix nanocomposites through powder metallurgy using graphene oxide nanosheets enhanced copper powders and spark plasma sintering

Enhanced interfacial bonding and mechanical properties of (TiC p +GNPs)/Cu composites by Ti-induced GNPs/Cu interfacial modification

Optimizing phase interface of titanium carbide-reinforced copper matrix composites fabricated by electropulsing-assisted flash sintering

Superior strength-ductility combination in TiC/TC4 composites via In situ construction Ti 2 Cu nanoparticles

Experimental and optimization studies of friction stir processed Cu-TiB2 surface composites

Self-lubricating behavior caused by tribo-oxidation of Ti3SiC2/Cu composites in a wide temperature range

In Situ Synthesis and Tribological Characterization of TiC–Diamond Composites: Effect of the Counterface Material on Wear Rate and Mechanism

Achieving high strength and superior wear‐resistant properties in TiH2 matrix reinforced with graphene nanoplates

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Enhancement of Tribological Properties in Siliconized Graphite Via Hierarchically Hybrid SiC/C Composite

Regulating the mechanical properties and electrical conductivity of CNTs/Cu composites by tailoring nano-sized TiC on the surface of intact CNTs

Study on the Tribological Properties of Carbon Fabric/Polyimide Composites Filled with SiC Nanoparticles

On the tribological behaviors of Cu matrix composites with different Cu-coated graphite content