Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Effect of Precipitation During Quenching on the Prediction of the Mechanical Properties of Al-5 Pct Cu Alloy after T6 Treatment

Precipitation Modeling and Validation of Al–5%Cu–0.4%Mn Alloy Using Quench Factor Analysis

Effect of quenching rate and its coupling model on precipitation and strength of Al–Cu–Cd alloys

Residual stress and precipitation of Mg-5Zn-3.5Sn-1Mn-0.5Ca-0.5Cu alloy with different quenching rates

A Comparative Study on Precipitation Behavior of a Sand-Cast Al–Li–Cu Alloy with the Different Quenching Rates

Constitutive Behavior for Quenching of Al–Cu–Mg Alloy With Consideration of Precipitation

Effects of Segregation, Quenching Rate, and External Stress on Precipitation Behaviors of Al-Cu-Cd Alloys

The effect of quenching rates on microstructure and mechanical properties of an Al-Si-Cu-Mg alloy

Competitive Relationship Between Thermal Effect and Grain Boundary Precipitates on the Ductility of an As-Quenched Al–Cu–Mn Alloy

Control of precipitates in CuCrZr alloy

Precipitated phase characteristics and fracture behaviour of cast Al–Cu–Mn alloy

Experimental and Simulation Study for the Influence of Thermal Pre-Deformation on Subsequent Aging Precipitation Kinetics of Al-Zn-Mg-Cu Alloy

Modeling the Precipitation Kinetics and Tensile Properties in Al-7si-Mg Cast Aluminum Alloys

Effects of aging treatment on the precipitation behaviors and mechanical properties of Al-5.0Mg-3.0Zn-1.0Cu cast alloys

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Influence of Quench-Induced Precipitation on Aging Behavior of Al-Zn-Mg-Cu Alloy

Review of the Quench Sensitivity of Aluminium Alloys: Analysis of the Kinetics and Nature of Quench-Induced Precipitation

Experiment and multiscale modeling of the coupled influence of constituents and precipitates on the ductile fracture of heat-treatable aluminum alloys

A Precipitation Hardening Model for Al-Cu-Cd Alloys

Temperature-dependent Constitutive Behavior with Consideration of Microstructure Evolution for As-Quenched Al-Cu-Mn Alloy

Influence of Cu content on the hardenability of Al-xCu-1.1Li alloys