Hydride-Induced Responses in the Mechanical Behavior of Zircaloy-4 Sheets

Hsiao-Ming Tung,Tai-Cheng Chen

DOI: https://doi.org/10.3390/met14020177

IF: 2.695

2024-02-02

Metals

Abstract:This study aimed to investigate the impact of hydrogen content, up to 1217 ppm, on the mechanical properties of Zircaloy-4, with a particular focus on the formation and impact of hydrides. Tensile specimens were tested across a range of temperatures and hydrogen concentrations. The results revealed a pronounced ductile-to-brittle transition associated with hydride formation. When the hydrogen content in the specimens ranged between 700 and 850 ppm, a ductile-to-brittle transition was observed at temperatures of 25 °C, 50 °C, and 75 °C. At 25 °C, the ultimate tensile strength (UTS) of Zircaloy-4 linearly increased as the hydrogen concentration rose from 0 to 1217 ppm H. However, at higher temperatures, the behavior of UTS became more complex, especially in the hydrogen concentration ranges of 500–850 ppm H. Elongation (EL) in the hydrided specimens was affected by both temperature and hydrogen concentration. As hydrogen concentration increased, there was a noticeable decline in uniform EL, while non-uniform EL showed even more significant reductions. Scanning electron microscopy (SEM) analysis of the fracture surfaces revealed that quasi-cleavage features became evident when the hydrogen content reached 850 ppm H, across all tested temperatures. These findings not only provide a quantitative assessment of the safety implications of Zircaloy-4 in nuclear reactor applications but also highlight the importance of the hydrogen charging process and mechanical testing in understanding its mechanical behavior.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to study the effect of different hydrogen contents (up to 1217 ppm) on the mechanical properties of Zircaloy-4 alloy, with a particular focus on the formation of hydrides and their impact. The study reveals a significant ductile-to-brittle transition phenomenon associated with hydride formation through tensile tests conducted at different temperatures and hydrogen concentrations. This transition was observed at temperatures of 25°C, 50°C, and 75°C when the hydrogen content in the samples ranged between 700 and 850 ppm. At 25°C, the ultimate tensile strength (UTS) of Zircaloy-4 increased linearly as the hydrogen concentration increased from 0 to 1217 ppm. However, at higher temperatures, the behavior of UTS became more complex, especially in the hydrogen concentration range of 500–850 ppm. Additionally, the elongation (EL) of hydrogenated samples was influenced by both temperature and hydrogen concentration. As the hydrogen concentration increased, the uniform elongation significantly decreased, while the non-uniform elongation showed a more pronounced reduction. Scanning electron microscope (SEM) analysis indicated that quasi-cleavage features appeared on the fracture surfaces at all test temperatures when the hydrogen content reached 850 ppm. These findings not only provide insights into the safety assessment of Zircaloy-4 in nuclear reactor applications but also emphasize the importance of the hydrogen charging process and mechanical testing in understanding its mechanical behavior.