Abstract:Zircaloy-4 is used as a fuel cladding material for water reactors, as it has good mechanical properties, corrosion resistance, and a low thermal neutron absorption cross section. However, the mechanical performance of Zircaloy-4 can be reduced during service due to hydrogen uptake and hydride formation. These hydrides are brittle, and often reduce the strength and toughness of materials as well as increase susceptibility to delayed hydride cracking (DHC). In this work, large grain Zircaloy-4 with hydrides was prepared and then cross sectioned using cryo-ion beam polishing, using plasma focused ion beam (pFIB) and broad ion beam (BIB) approaches to enable the preparation of a very high quality flat surface with no preferential etching of either the hydride or zirconium metal (typically metallographic polishing preferentially removes hydrides). Conventional and high angular resolution electron backscatter diffraction (EBSD) analysis were then used to explore morphology, deformation fields, and orientation relationships between the zirconium matrix and hydrides. Four maps were collected for analysis which included hydrides near grain boundaries: (a) where the hydride smoothly decorates across two of the connecting boundaries near a triple junction; (b) where the hydride smoothly decorates the boundary; (c) a mixture of smooth decoration of the interface and protrusion into the grains; (d) fine scale hydride that protrudes into one grain. This work highlights that incompatibility of the hydride within the zirconium matrix is strongly linked to the orientation relationship of the hydride and matrix, and the grain boundary character. These results may enable enhanced understanding of the role of hydrides in fracture as well as stress-induced hydride reorientation and DHC susceptibility.

Hydrogen in zirconium alloys: A review

Mechanisms of Hydride Nucleation, Growth, Reorientation, and Embrittlement in Zirconium: A Review

Corrosion of Zirconium Alloys Used for Nuclear Fuel Cladding

Hydride growth mechanism in zircaloy-4: Investigation of the partitioning of alloying elements

Nano Hydride Precipitation-Induced Disappearance of Yield Drop in Zirconium Alloy at Elevated Temperature

Influence of kinetic effects on terminal solid solubility of hydrogen in zirconium alloys

Hydride precipitation dependence on α-parent orientation and plastic deformation in zirconium alloys

The role of hydrogen in zirconium alloy corrosion

Hydrogen diffusion and precipitation under non-uniform stress in duplex zirconium nuclear fuel cladding investigated by high-resolution neutron imaging

Modeling and tests on the damage and fracture behaviors of non-irradiated zirconium alloys with different hydrogen concentrations at RT and 350°C

Effect of hydride orientation on tensile properties and crack formation in zirconium alloy cladding tubes

Effect of Heating Rate on Hydride Reorientation Behavior of Zirconium Alloy Tubes under Non-Stress Loading

Hydrogen diffusion in zirconium hydrides from on-the-fly machine learning molecular dynamics

Revealing the role of hydrogen content on the mechanical behavior and cracking mechanisms of Zircaloy-4 under strain

High-throughput Computing for Hydrogen Transport Properties in Ε-Zrh2

Evidence of hydrogen trapping at second phase particles in zirconium alloys

Investigation of δ zirconium hydride morphology in a single crystal using quantitative phase field simulations supported by experiments

On the interaction of grain-scale and hydride-scale stresses in hydrogen enriched zirconium alloy nuclear cladding via combined discrete dislocation plasticity and crystal plasticity finite element modelling

Hydrogen Permeation Characteristic of Nanoscale Passive Films Formed on Different Zirconium Alloys

Exploring the Hydride-Slip Interaction in Zirconium Alloys

Characterization of local deformation around hydrides in Zircaloy-4 using conventional and high angular resolution electron backscatter diffraction