Effects of Sb Content on Solidification Pathways and Grain Size of AZ91 Magnesium Alloy

Dan-Hui Hou,Song-Mao Liang,Rong-Shi Chen,Chuang Dong,En-Hou Han

DOI: https://doi.org/10.1007/s40195-014-0178-4

2014-01-01

Acta Metallurgica Sinica (English Letters)

Abstract:The phase constitution and solidification pathways of AZ91 + x Sb ( x = 0, 0.1, 0.5, 1, in wt%) alloys were investigated through ways of microstructure observation, thermal analysis technique, and thermodynamic calculation. It was found that the non-equilibrium solidification microstructure of AZ91 + x Sb ( x = 0.1, 0.5, 1) is composed of α-Mg matrix, β-Mg 17 Al 12 phase, and intermetallic compound Mg 3 Sb 2 . The grain size of the alloys with different Sb contents was quantitatively determined by electron backscattered diffraction technique which shows no grain refinement in Sb-containing AZ91 alloy. Thermodynamic calculations are in reasonable agreement with thermal analysis results, showing that the Mg 3 Sb 2 phase forms after α-Mg nucleation, thus impossible acts as heterogeneous nucleus for α-Mg dendrite. Besides, the solid fraction at dendrite coherency point ( f s DCP ) determined from thermal analysis decreases slightly with increasing Sb content, which is consistent with the fact that Sb does not refine the grain size of AZ91 alloy.