The effect of Zn content on the microstructure and mechanical properties of the Al-mg-Si alloy

Xuehong Xu,Wenbo Zhu,Manfa Yuan,Chaojie Liang,Yunlai Deng

DOI: https://doi.org/10.1016/j.matchar.2023.112714

IF: 4.537

2023-02-06

Materials Characterization

Abstract:In the present study, the influence of Zn content on the microstructure and mechanical properties of the Al-Mg-Si alloy is systematically investigated. The results show that the precipitation sequence within the grains of the alloy does not change when Zn content does not exceed 2.0 wt%. The intragranular precipitates are mainly composed of β" precipitates with a small amount of η' precipitates when Zn content reaches 4.0 wt.%. Zn addition does not affect the precipitation sequence along the grain boundaries of the alloy when Zn content does not exceed 1.0 wt.%. But the grain boundary precipitates (GBPs) transform into Zn-rich phases when Zn content increases to 2.0 wt.%. The strength of the alloy firstly gradually improves and then reduces when Zn content increases to 2.0 wt.%. This is mainly due to the effect of Zn content on the distribution of the intragranular precipitates. The strength of the alloy significantly enhances again as a result of the increase of the number density of β" precipitates and the formation of η' precipitates when Zn content reaches 4.0 wt%.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing