Abstract:To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures (200, 250, 300 and 350 ℃), while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum (with a range average of 235 MPa) and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.

Effect of Sm content on microstructure and properties of extruded Mg-6Al-2Sr alloy

Effect of Sm on the Microstructure and Mechanical Property of Mg-Xsm-0.4zn-0.3zr Alloys

Effect of Sm on Microstructures and Mechanical Properties of Mg-10Gd-0.5Zr Alloy

Effect of Sm Addition on the Microstructure and Mechanical Properties of Mg–xSm–0.4Zr Alloys

Effects of Sm on Microstructure and Mechanical Properties of Mg-5.5al-0.5y Alloy

Effect of Sm on Microstructure, Mechanical Property and Lattice Constant of As-Cast Mg–11Gd–2Y–0.6Al Alloy

Effects of Sm Addition on Microstructure and Mechanical Properties of Mg–6Al–0.6Zn Alloy

Effects of Sm Addition on Microstructure and Mechanical Properties of A Mg-10y Alloy

Effect of Sm on microstructures and mechanical properties of Mg-Gd(-Sm)-Zr alloys by hot extrusion and aging treatment

Effects of Samarium Content on Microstructure and Mechanical Properties of Mg–0.5Zn–0.5Zr Alloy

Influence of Sm addition on microstructural and mechanical properties of as-extruded Mg–9Li–5Al alloy

Effects of Sm content on microstructures and mechanical properties of casting Mg-Y-Nd-Sm-Zr alloys

Effects of Sm on the Grain Refinement, Microstructures and Mechanical Properties of AZ31 Magnesium Alloy

Microstructure and Texture Evolution with Sm Addition in Extruded Mg–Gd–Sm–Zr Alloy

Microstructure and Mechanical Properties of Mg-Gd-Y-Sm-Al Alloy and Analysis of Grain Refinement and Strengthening Mechanism

Thermal Conductivity and Mechanical Properties of Sm-containing Mg-Zn-Zr Alloys

Effects of Sm on Microstructure and Mechanical Properties of AZ61 Alloys

Effect of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg−8Li−3Al−(1,2,3)Sn alloys

Effect of Sr on Microstructure and Mechanical Properties of Mg-9Li-3Al Alloy

The influences of Sr on the microstructure and mechanical properties of Mg-5Zn-2Al alloy

Influence of Extrusion on the Microstructure and Mechanical Behavior of Mg-9li-3al-Xsr Alloys