Abstract:During plasma spraying, SiC particles undergo sublimation, accompanied by the sublimation and decomposition of Si and C atoms in the crystal lattice. Ultimately, the deposited SiC either spreads splash or breaks apart on the surface of the carbon‐carbon composite matrix. It is widely known that silicon carbide (SiC) is challenging to thermal spray. However, the nature of deposition and the underlying mechanisms are still not clearly understood. In the current work, the process of atmospheric plasma‐sprayed SiC was investigated in detail. SiC exhibits sublimation severely under the plasma spraying (PS). More than 65 mol.% SiC particles lost by sublimation during PS estimated by calculation. Due to the nonuniformity of temperature in plasma flame, a small amount of SiC particles was retained. Moreover, a small amount of Si and SiO2 was experimentally observed after deposition process from the single‐splat characterization. According to the first‐principles calculations, the detachment energy of C atom from the lattice (0.591 eV) is lower than that of Si atom (1.257 eV). The adsorption energies of an O atom on the Si‐ and C‐terminated surfaces are −9.549 and −7.631 eV, respectively. Therefore, C is more likely to form gaseous products after decomposition, and Si is more likely to be retained to form Si and SiO2. Mullite was found on the grain boundaries of molten Si, which was attributed to the rapid diffusion of the Al2O3 substrate along the grain boundaries of Si, promoting the spreading of molten splats. It is difficult to stack particles through self‐diffusion among SiC particles to form coatings. The discovery on thermal deposition mechanism of SiC in PS is helpful to promote the practical application of SiC coatings on preparation optimization and interfacial bonding improvement.

Preparation and Ablation Properties of Y 2 SiO 5 Coating for SiC-Coated C/C Composites by Supersonic Plasma Spraying

Microstructures and Phases of Ytterbium Silicate Coatings Prepared by Plasma Spray-Physical Vapor Deposition

Spraying Power Effect on Micro-Structure and Mechanical Property of TaSi2 Coating Prepared by Supersonic Air Plasma Spraying for SiC-Coated C/C Composites

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Plasma sprayed TiC–Ti5Si3–Ti3SiC2 composite coatings from Ti–SiC-graphite powders with different SiC particle size

Ablation Mechanism and Elevated Ablation Resistance of In-Situ Zrc-Zrsi2 Composite Coating Prepared by Plasma Spraying

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Ablation Resistance of APS Sprayed Mullite/ZrB2-MoSi2 Coating for Carbon/Carbon Composites

Deposition behavior and mechanism of thermal sprayed SiC

Effect of Submicron and Nano SiC Particles on Erosion Wear and Scratch Behavior of Plasma-Sprayed Al 2 O 3 /8YSZ Coatings

Preparation and characterization of monolayer oxidation resistant coating on C/SiC composites

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Synthesis of In Situ ZrB2-SiC-ZrC Coating on ZrC-SiC Substrate by Reactive Plasma Spraying

Effects of SiC on microstructure and properties of plasma sprayed ZrB2–ZrC composite coating

Investigation of Yb2SiO5/BSAS/Si coating on Cf/SiC composites: processing and steam corrosion behavior

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

Phase and microstructure evolutions of in-situ ZrC composite coating under plasma torch ablation