The Effect of Rare Earth Y on the Inhibitor Precipitation Behavior of Strip‐Cast Grain‐Oriented Silicon Steel

Shun Wang,Yang Wang,Yuanxiang Zhang,Feng Fang,Erliang Zhang,Xiaoming Zhang,Guo Yuan
DOI: https://doi.org/10.1002/srin.202400022
IF: 2.1258
2024-05-02
steel research international
Abstract:The addition of trace rare earth Y to the strip‐cast grain‐oriented silicon steel can promote the rapid precipitation of AlN inhibitors. The doped Y atoms tend to segregate at the Al–N interface and reduce the precipitated interface energy. 0.3 mm‐thick grain‐oriented silicon steel sheets with varying Y contents are produced via twin‐roll strip‐casting and two‐stage cold rolling process. This study primarily investigates the evolution of microstructure, texture, and precipitation along the processing. Specifically, the effect of rare earth Y on second‐phase particle precipitation in ultralow carbon grain‐oriented silicon steel is examined. Results indicate that higher Y content will consume beneficial inhibitor elements such as S and N, leading to the formation of coarse rare earth inclusions (≈10 μm) in the cast strip. This significantly diminishes inhibition ability and magnetic induction (B8 = 1.58 T≈1.71 T). On the contrary, the addition of trace Y can accelerate the precipitation of inhibitors. During the intermediate annealing stage, steel with trace Y exhibits a significant enhancement in precipitate distribution density (from 2.8 μm−2 to 13.6 μm−2), and the final magnetic induction B8 increases from 1.86 T to 1.91 T compared to steel without Y. In addition, the results of first‐principle calculations based on density functional theory reveal that the doped Y atom prefers to segregate at the Al–N interface, and the interface energy reduces from 1.871 J m−2 to 1.024 J m−2, thereby promoting the precipitation of AlN.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?