Abstract:1. Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz and a TCF∼−14ppm∘C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. 2. The 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics have excellent temperature stability. 3. The 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramics doped with LiF and LBSCA glass are suitable for LTCC technology due to their low sintering temperatures (from 830°C to 890°C) and good chemical compatibility with silver. In this work, the 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics were synthesized using a standard solid‐phase reaction process, and the inherent relationship between crystal structure and microwave dielectric properties was thoroughly explored. The crystal structure of the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic was determined by X‐ray diffractometer, which confirmed the existence of two phases. Microstructure observation of the ceramics was obtained by scanning electron microscope (SEM). Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz, and the temperature coefficient of resonant frequency (TCF) ∼−14 ppm°C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. By adding sintering additives LiF and Li2O–B2O3–SiO2–CaO–Al2O3 (LBSCA) glass, the sintering temperature was decreased from 1060°C to 870°C. Good microwave dielectric properties with a ԑr ∼6.59, a Q × f ∼18 820 GHz, and TCF ∼−14 ppm°C−1 were achieved in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ‐2 wt.% LiF, 1 wt.% LBSCA (2F1LBSCA) ceramic sintered at 870°C. The low‐temperature firing ceramics could also be well co‐fired with Ag with good chemical compatibility. These results indicated that the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic with 2F1LBSCA additions can be utilized in low‐temperature co‐fired ceramics technology to produce high‐frequency communication components.

Microwave Dielectric Properties of MLi2Ti6O14 [M=Ba and Sr] Ceramics and Their Compatibility with Sliver

Microwave Dielectric Properties of Temperature Stable (1-X)srlaalo4-xtio2 Composite Ceramics

Effects of (mg1/3nb2/3) Substitution on the Structure and Microwave Dielectric Properties of Sr2TiO4 Ceramics

Influence of V substitutions on sintering behaviors and microwave dielectric properties of Ba4LiNb3O12 ceramic

Microwave dielectric properties of Li2WO4-added SrWO4 ceramics for LTCC applications

Sintering behavior, structural evolution, and dielectric properties of Li2+MgTiO4F microwave dielectric ceramics

Microstructure and Dielectric Properties Control of Ba4(Nd0.7Sm0.3)9.33Ti18O54 Microwave Ceramics

A new low-loss SrLaMgTaO6 microwave dielectric ceramic with cubic structure

Evolution of Phase Transformation on Microwave Dielectric Properties of BaSixO1+2x Ceramics and Their Temperature-Stable LTCC Materials

Low temperature sintered Li6MgTiNb1-xVxO8F microwave dielectric ceramics with high-quality factor

Microwave dielectric properties of SrLa[Ga<sub>1-<i>x</i></sub>(Mg<sub>0.5</sub>Ti<sub>0.5</sub>)<i><sub>x< /sub></i>]O<sub>4</sub> and SrLa[Ga<sub>1-<i>x</i></sub>(Zn<sub>0.5</sub>Ti<sub>0.5</sub>)<i><sub>x< /sub></i>]O<sub>4</sub> (<i>x</i>=0.2-0.8) ceramics

Microwave Dielectric Properties of (1-X)(ca<sub>0.61</sub>nd<sub>0.26</sub>)tio<sub>3</sub>–x(li<sub>0.5</sub>sm<sub>0.5</sub>)tio<sub>3</sub>

Low temperature sintering and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics for LTCC applications

Microwave Dielectric Properties of Low-Fired Li2TiO3–MgO Ceramics for LTCC Applications

Microwave Dielectric Properties of (1-x)(Ca0.61Nd0.26)TiO3–x(Li0.5Sm0.5)TiO3

Structure and Microwave Dielectric Properties of SrLa[Al1−x(Mg0.5Ti0.5)x]O4 (x = 0.2–0.8) Ceramics

Effect of excess lithium on the structure and microwave dielectric properties of LiMg0.5Ti0.5O2 ceramics

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Sintering behavior and microwave dielectric properties of Sr2CeO4 ceramics doped with Li2CO3-Bi2O3

Structure, bond features, and microwave dielectric properties of Li2(Mg1−xCax)2(MoO4)3 ceramics for ULTCC application

Effect of LiF and LBSCA glass on the microwave dielectric properties of 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics for LTCC applications