Abstract:As the feature size of integrated circuit (IC) shrinks down to 28nm and below, Aluminum (Al) is considered to be one of the suitable gate materials. During chemical mechanical polishing (CMP) of the Al gate, Al is very easy to be scratched. The purpose of Al gate polishing is to achieve effective removal and improve surface quality. The pH value and additives of slurry are critical factors affecting the material removal rate and the surface quality. Taking the advantage of enhancing chemical action and solubility of product in CMP process, the potentio dynamic polarization measurements with dynamic impedance monitoring were performed to evaluate the effects of pH value and glycine on the behavior of the electrochemical corrosion. The results showed that the corrosion potential decreased as the pH value and glycine concentration increased. Meanwhile, the dissolution rate and reversing proportion to the polarization resistance increased with the increasing of pH value and glycine concentration, the removal rate of by-products (Al(OH) 3) from the interfacial reaction accelerated, and the chemical adsorption of NH2- group identified by FTIR was converted into a soluble form, the removal rate was increased from 216 angstrom/min to 594 angstrom/min, and the surface roughness was greatly reduced from 18.6nm to 1.57nm. The synergetic effects of pH and glycine, combined with the analysis of the EIS for the aluminum alkaline CMP, indicated the RR and the surface quality of aluminum after CMP was obviously improved due to the chemical dissolution efficiency of interfacial by-product enhanced. (c) The Author(s) 2019. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org.

Electro-corrosion Machining of Aluminum in Alkaline Solution and Passivated Mechanism

Electrochemical behaviour of aluminum in alkaline solution

The Corrosion and Electrochemical Behaviour of Pure Aluminium in Alkaline Methanol Solutions

Influence of Acid Pickling on Electrodeposition of Aluminum on Magnesium Alloy in Room Temperature Molten Salts

Study on oxidation mechanism of aluminum surface under applied electric field

Comparative Study on Electrochemical Behavior of AlLi Alloy 2 A 97 Machined Surfaces in Sodium Chloride Solution

Electrochemical Corrosion Behaviour of Microcrystalline Aluminium in Acidic Solutions

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Mechanistic aspects of electrochemical corrosion of aluminum alloy in ethylene glycol–water solution

Electrochemical noise features of pure aluminum during pitting corrosion in neutral NaCl solution

Electrochemical Behavior of Aluminum in Grignard Reagents/thf Electrolytic Solutions for Rechargeable Magnesium Batteries

Effect of Ph Value and Glycine in Alkaline CMP Slurry on the Corrosion of Aluminum by Electrochemical Analysis

Effect of Electrolytic Parameters on Surface Morphology and Microstructure of 2A12 Al Alloy

In Situ Electrochemical Monitoring of the Crevice Corrosion Process of the 7075-T651 Aluminium Alloy in Acidic NaCl and NaNO3 Solution

Electrochemical Polishing of 7075 Al Alloy in Phosphoric Acid

Electrochemical study of active dissolution for aluminum in neutral NaCl solution

Anodic Electrochemical Behaviors of 2219 Aluminum Alloy in NaNO 3 and NaCl Electrolytes

Generation of surface texture on 2A50 aluminum alloy with electrochemical micromachining for tribological application

Electrochemical Properties of Aluminum Anode in Alkaline Organic Solution

Electrochemical Noise Study on 2024-T3 Aluminum Alloy Corrosion in Simulated Acid Rain under Cyclic Wet–dry Condition

Electrochemical Machining of Super-Hydrophobic Al Surfaces and Effect of Processing Parameters on Wettability