Abstract:A novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. Firstly, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3‐Al2O3‐SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints. In this work, a novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. First, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3–Al2O3–SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The content of Al2O3 in the composite interlayer reached 52.7%. As a result, the coefficient of thermal expansion mismatch between the interlayer and the alumina ceramic was reduced to only 2%. The flexural strength of the joints at room temperature was equivalent to that of the alumina ceramic. Furthermore, the flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints.

Joining of Al 2 O 3 by epitaxial growth of aluminum borate whiskers for high-temperature applications

Microstructure Evolution of Alumina/Alumina Joint Bonded by Boron Oxide–Alumina Nonmetal Powder Interlayer

Surface Synthesis of Aluminum Borate Whiskers on the ZTA Ceramics and Its Application to Joining

Epitaxial Growth of Aluminum Borate Whiskers and Simultaneous Joining of Alumina Ceramics Via a Sol–gel Method

Joining ZTA Ceramics by Using Whiskers Reinforced Borosilicate Glasses for High-Temperature Applications

Joining of Al2O3 to ZTA Using a B2O3–Al2O3–SiO2 Glass with In-Situ Precipitated Whiskers

Joining Alumina And Sapphire By Growing Aluminium Borate Whiskers In-Situ, And The Whiskers' Orientation Relationship With The Sapphire Substrate

Microstructure Evolution During Air Bonding of Al2O3 to Al2O3 Joints Using Bismuth–borate–zinc Glass

Crystallization and Wetting Behavior of Bismuth–borate–zinc Glass and Its Application in Low Temperature Joining Alumina Ceramics

Temperature-Dependent Transformation from Whisker- to Nanoparticle-Strengthened Composite Interface in the Al2o3/Ag-Based Alloy System and Mechanical Properties of the Joints

Synthesis and microstructural characterization of aluminum borate whiskers

Low-temperature Brazing of Alumina Ceramics with Bismuth-Borate Glass in Air

Alumina ceramics joined with screen-printed B2O3 by spark plasma sintering

Novel two‐step method for joining alumina ceramic by using Al2O3 powder followed by glass infiltration

Wetting of Microstructured Alumina Fabricated by Epitaxial Growth of Al 4 B 2 O 9 Whiskers

Joining of Al2O3 Ceramics at Low Temperature

Microstructure and Strength of Al2o3/Al2o3 Joints Bonded with Zno-Al2o3-B2o3-Sio2 Glass-Ceramic

A Composite Structural High-Temperature-resistant Adhesive Based on In-Situ Grown Mullite Whiskers

On the Thermal Stability of Coating in an Al18B4O33w/α-Al2O3/6061Al Composite

Aluminum borate whisker-based lattices with a hierarchical pore structure obtained via digital light processing

Bonding Mechanisms and Shear Properties of Alumina Ceramic/Stainless Steel Brazed Joint