Abstract:Porosity-controllable TiO2 nanocrystallines with pure anatase phase have been synthesized through a salt-leaching assisted sol-gel method, where glycerol was used as the dispersant to disperse the inorganic precursor (tetrabutyl titanate, TBT) and the chelating ligand to attenuate the hydrolysis/condensation reaction kinetics, while the salts (NaCl) were used as porosity-induced agents to produce pores in the final titania products when the salts leached out. The porosities and surface areas of obtained titania samples could be adjusted by altering the NaCl concentration in the precursor sol, which was examined by experimental techniques such as XRD, TEM and Brunauer-Emmett-Teller (BET) nitrogen adsorption-desorption. In addition, their photocurrent actions and photocatalytic abilities were also investigated so as to address the relationship between the nanostructures and their photoelectrochemical properties. It was demonstrated that the obtained titania samples exhibited different photocurrent actions and photocatalytic activities due to their different morphologies, particle sizes, surface areas as well as pore architectures. Therefore, the salt-leaching assisted sol-gel method described herein offers a new effective and facile strategy for the preparation of pure anatase TiO2 nanocrystallines with adjustable porosity, as well as provides the titania products with specific photoelectrochemical properties for applications in a variety of areas such as photovoltaic cells, photocatalysis and so on.

Towards Ultrafine Tio2 Nanocrystal at Room Temperature

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

A Simple Solution-Phase Route for Room-Temperature Synthesis of Mesoporous and Nanocrystalline Anatase Tio2

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

pH control on preparation of nano-TiO_2 by gel-sol process

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

Synthesis of Nanocrystal Titania Sol with Different Ratio of Rutile and Anatase at Low Temperature

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Synthesis of Controllable Crystalline Nano-Tio2 at Low Temperature

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase

Synthesis of Size-Controlled Nanotitania Particles via a Simple Sol-Gel Method

Synthesis Of Nanocrystalline Tio2 By A Salt-Leaching Assisted Sol-Gel Method And Their Photoelectrochemical Properties

Synthesis of Crystalline Nanosized Titanium Dioxide Via a Reverse Micelle Method at Room Temperature