Microstructure and Property Evolution of Cu90Zr10 Alloy in the Process of Mechanical Alloying

C. J. Li,L. Teng,J. Tan,Q. Yuan,J. J. Tang,T. L. Chen,X. K. Zhu
DOI: https://doi.org/10.4028/www.scientific.net/amr.750-752.667
2013-01-01
Advanced Materials Research
Abstract:Cu90Zr10 alloy powder was prepared by high-energy ball milling. The microstructure and property evolution of this alloy powder during mechanical alloying (MA) were investigated by using X-ray diffraction and optical microscopy (OM). The alloy powder with an average grain size of 10 - 40 nm was obtained, and the grain size was found to decrease gradually with increasing milling time. The microhardness reached a maximum value (about 295 Hv) after 30 h milling. The internal microstrain and the microhardness of the samples increased due to the grain refinement and solid solution during milling, and 10at.% Zr could be brought into Cu lattice by solid solution during MA. At last, the mechanisms of strengthening were discussed.