Abstract:Mechanical alloying (MA) has been used to fabricate the Co2FeAl Heusler alloy with a nanocrystalline structure. The formation mechanism of the alloy has been investigated. Rietveld analysis showed that all samples that were milled for more than 15 hours had an L21 structure with a space group of Fm3m. The crystallite size and internal strain of the samples were calculated using the Williamson-Hall equation. With mechanical alloying of up to 20 hours the crystallite size of Co2FeAl increased, after which the crystallite size started to decrease. In contrast, internal strain first decreased during the process and then increased with the increase of milling time. The powder obtained after 20 hours of MA was split into three parts and separately annealed at 300, 500 and 700 oC for 5 hours. A considerable increase was observed in the hardness value of powder particles with the increase of annealing temperature up to 500 oC. However, the hardness value of the sample annealed at 700 oC decreased. It seems that this feature is related to parameters such as increase of crystallite size, enhancement of lattice ordering, change in density of defects and impurities and nonstoichiometric effects.

What problem does this paper attempt to address?

This paper aims to explore how the microstructure and mechanical properties of materials evolve with the change of milling time and annealing temperature during the preparation of nanocrystalline Co₂FeAl Heusler alloy by mechanical alloying (MA) method. Specifically, the research focuses on the following aspects: 1. **Formation mechanism of Heusler phase**: Through X - ray diffraction (XRD) analysis, the phase composition changes of samples under different milling times were studied, especially the formation process of L2₁ structure and its space group (Fm3m). The research shows that after milling for more than 15 hours, all samples form Heusler phase with L2₁ structure. 2. **Changes in grain size and internal stress**: The changes in grain size and internal stress were calculated using the Williamson - Hall equation. The results show that as the milling time increases, the grain size first increases and then decreases; while the internal stress decreases in the initial stage and then increases with the extension of milling time. 3. **Effect of annealing treatment**: The powder after milling for 20 hours was divided into three parts and annealed at 300 °C, 500 °C and 700 °C for 5 hours respectively to study the effect of annealing temperature on the structure and mechanical properties. The results show that the increase of annealing temperature leads to the increase of grain size, the decrease of internal stress, and the hardness value of powder particles significantly increases as the annealing temperature rises from 300 °C to 500 °C, but the hardness value at 700 °C decreases. In summary, this research mainly solves the problem of how the microstructure and mechanical properties of materials are affected by milling time and annealing conditions during the preparation of Co₂FeAl Heusler alloy by mechanical alloying method, providing a theoretical basis for optimizing the preparation process of Heusler alloy.

Evolution of microstructural and mechanical properties of nanocrystalline Co2FeAl Heusler alloy prepared by mechanical alloying

Macro-micro Analysis of Mechanical Properties of Al0.6CoCrFeNi High-Entropy Alloy Particle-Reinforced Al-based Composites

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Structural and thermal properties of the Fe-based alloys prepared by mechanical milling

Microstructural and Magnetic Characteristics of High-Entropy FeCoNiMnTi Alloy Produced via Mechanical Alloying

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

Structural, magnetic and electron transfer effect of Cr additive on Fe 65 Co 35 nanopowder fabricated mechanical alloying

Microstructural evolution of CrCuFeNiZn nanocrystalline high entropy alloy prepared by mechanical alloying

Microstructure evolution and mechanical properties of CoCrFeNiAl0.3 high entropy alloy produced by ball milling in combination with thermomechanical consolidation

Synthesis and Phase Evolution of a Nanocrystalline FexCrNiAl (x = 1.0, 0.5, 0.25) High-Entropy Alloys by Mechanical Alloying

Microstructural Evolution and Mechanical Properties of Al0.5CoCrFeNi High-Entropy Alloy after Cold Rolling and Annealing Treatments

Microstructure of nano-crystalline material Al60Fe20Cu20

Effect of Milling Time on the Structure Stability of FeMnNiCrAl Non-equiatomic High-Entropy Alloy

Microstructure and Mechanical Property Evolution during Annealing of a Cold-Rolled Metastable Powder Metallurgy High Entropy Alloy

Microstructure and Mechanical Properties of Ultrafine Grained CoCrFeNi and CoCrFeNiAl0.3 High Entropy Alloys Reinforced with Cr2O3/Al2O3 Nanoparticles

Nano-Structure Evolution and Mechanical Properties of AlxCoCrFeNi2.1 (x = 0, 0.3, 0.7, 1.0, 1.3) High-Entropy Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Microstructure Evolution and Mechanical Properties of NiAlCrFeMo High Entropy Superalloy after Different Annealing Treatment

Nanostructured Al–Ti–Fe–Mn–Ni High-Entropy Alloy by Mechanical Alloying: Synthesis and Characterization

Effect of Aluminum Addition on the Microstructure, Magnetic, and Mechanical Properties of FeCrCoNiMn High-Entropy Alloy

Study of the effect of mechanical alloying on the structure of Ni-Mn-Sn Heusler alloy

Effect of Al on Microstructure and Mechanical Properties of Cast CrCoNi Medium-Entropy Alloy