Abstract:Elemental powder blends with atomic composition of Cu 100− x Ta x ( x =10, 30, 50, 70, and 90) were ball milled in a SPEX mill at several temperatures (room temperature (RT), liquid nitrogen temperature (LN 2 T), −80 °C, and 95 °C) to examine the effect of milling temperature on the extent of alloying and microstructural refinement. For the Cu-rich powders (10< x <50), high-energy ball milling to steady state at all temperatures produced a mixture of nanocrystalline Cu and Ta with no observable extension of mutual solid solubility. Compared with milling at RT, cryomilling (LN 2 T) caused further refinement of Cu crystallites, while the same steady-state grain size was reached for Ta crystallites. On the Ta-rich side (50< x <90), ball milling at all temperatures led to refined Cu and Ta grain sizes. Partial amorphization seemed to be present, which apparently increased in extent with increasing contamination from the milling media upon extended milling. Very similar results were obtained for milling at RT and LN 2 T. It was concluded that high-energy ball milling at LN 2 T did not drastically enhance the amorphization reaction between Cu and Ta nor extend their mutual solubility. The limited power of cryomilling to alloy immiscible elements such as Cu-Ta is explained as a consequence of the inability to fully suppress, during energetic collisions, the atomic mobility responsible for phase separation even when the milling is conducted at the nominal LN 2 T. The temperature dependence of milling-induced microstructural refinement and alloying is analyzed in terms of the dynamics of the generation and annihilation of the nonequilibrium vacancies in an externally driven system. It is predicted that externally forced mixing as well as diffusion assisted by high-energy ball milling can be merely weakly temperature dependent between RT and LN 2 T. As a result, the extension of solubility by using cryomilling is feasible only in limited systems, and this process cannot be expected to alloy all immiscible elements.

Effect of Temperature on Mechanical Alloying of Cu-Zn and Cu-Cr System

Temperature Effect on Mechanical Alloying of Cu-Zn Binary

The Effect of A Small Amount of Tungsten on the Microstructure of Mechanically Alloyed Ag37cu63

Temperature Effect on Mechanical Alloying of Cu-5% Cr Powder

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Amorphization of Zr–Al Solid Solutions under Mechanical Alloying at Different Temperatures

Amorphization Of Zr-Al Under Mechanical Alloying At Different Temperatures: A Re-Entrant Melting Phenomenon

Mechanical Alloying of Copper-Zinc Powders at Cryogenic Conditions

Effect of milling temperature on mechanical alloying in the immiscible Cu-Ta system

Low-Temperature Mechanical Alloying of Cu-Fe and Cu-Ta Powders

Mechanical Alloying of the Immiscible Cu-60wt%Cr Alloy: Phase Transitions, Microstructure, and Thermodynamic Characteristics

Formation of nanocrystalline and amorphous phase of Al-Pb-Si-Sn-Cu powder during mechanical alloying

Effects of milling process parameters and PCAs on the synthesis of Al0.8Co0.5Cr1.5CuFeNi high entropy alloy powder by mechanical alloying

Effect of Metastable Cr(Mo)s/Cr(Mo)a Powders on Mechanical Alloying the Immiscible Cu–Mo–Cr System

Influence of Zr Microalloying on the Microstructure and Room-/High-Temperature Mechanical Properties of an Al–Cu–Mn–Fe Alloy

Study on Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying

Effect of temperature on mechanical properties of Al0.5CoCrCuFeNi wrought alloy

Effect of temperature on mechanical behavior of Cu–Cr–Co–Ti alloys

Effect of Aging and Ball Milling on the Phase Transformation of Ni50Mn25Ga17Cu8−xZrx Alloys

Effect of elevated-temperature annealing on microstructureand properties of Cu−0.15Zr alloy

Phase Transformation Characteristics Of Cu-Cr And Cu-Mo Binary Alloys During Mechanical Alloying