Abstract:The corrosion behavior of the 70/30 Cu–Ni alloy in stagnant, aerated pristine and sulfide-containing simulated seawater as a function of exposure time was investigated with polarization curve measurement and electrochemical impedance spectroscopy (EIS). It was demonstrated that the compact protective oxide film formed on the 70/30 Cu–Ni alloy resulted in the decrease of corrosion rate in aerated pristine seawater; while the corrosion rate of 70/30 Cu–Ni alloy in aerated sulfide-containing seawater increased dramatically due to the catalysis of the sulfide ions or sulfide scale for both the cathodic and anodic reactions. The impedance spectra and the corresponding equivalent circuits confirmed that a duplex layer of a surface film was formed on the 70/30 Cu–Ni alloy in aerated pristine seawater after a period of time and that the inner layer was responsible for the good resistance of the alloy; while only a porous and non-protective corrosion product layer formed on the 70/30 Cu–Ni alloy in aerated sulfide-containing seawater, which made small values of charge transfer resistance (Rct) to last for a abnormally long time by interfering with the growth of the protective oxide film. The composition of the surface film on the alloy in pristine and sulfide-containing seawater for different exposure times were investigated thoroughly by XPS. It was found that the duplex corrosion product layer formed on the alloy in pristine seawater was composed of an inner Cu2O and an outer CuO layer. The porous and non-protective corrosion product layer formed on the alloy in aerated sulfide-containing seawater was a mixture of CuCl, Cu2S, NiS, Cu2O and NiO with trace amounts of CuO and Ni(OH)2 and that the most significant component was Cu2S. In addition, SEM was used to analyze the topography of the 70/30 Cu–Ni alloy in both solutions after different exposure times.

The Corrosion Behavior of Cu-Ni-Si Alloy in Sea Water with Deep-Sea Bacteria

Electrochemical Corrosion Behavior of Cu-15Ni-8Sn Alloy in Marine Microbial Medium

Corrosion Behavior and Mechanism of a Cu-Ni Alloy in Marine Environment

Corrosion Behavior of Cupronickel Alloy in Simulated Seawater in the Presence of Sulfate-Reducing Bacteria

Corrosion of Copper-Nickel Alloys in Seawater-Based Electrolytes

Long-Term Corrosion Behavior of Cu-10Ni and Cu-20Ni Alloys in Simulated Seawater

Surface characterization and corrosion behavior of 70/30 Cu–Ni alloy in pristine and sulfide-containing simulated seawater

ELECTROCHEMICAL CORROSION BEHAVIOR OF 90/10 Cu-Ni ALLOY IN FLOWING SEAWATER

Accelerated Corrosion Behavior Of B10 Cu-Ni Alloy In Seawater

Corrosion Behavior of Ultra-high Strength Steel 23co14ni12cr3mo in Simulated Seawater Environment

The Influence of the Marine Aerobic Pseudomonas Strain on the Corrosion of 70/30 Cu-Ni Alloy

Insight to corrosion mechanism of 90/10 copper-nickel alloys under different sea depths

Seawater corrosion of A Cu-Ni alloy in intermittent immersion

Studies on Sulfate Reducing Bacteria Influenced Corrosion of 90/10 Cu/Ni Alloy

Influence of Deformation and Heat Treatment on Seawater Corrosion of 70Cu-30Ni Alloy

Clarifying the effect of Cu element on the corrosion properties of Ni-Mo low alloy steel in marine environment

Biogenic H2S and Extracellular Electron Transfer Resulted in Two-Coexisting Mechanisms in 90/10 Cu-Ni Alloy Corrosion by a Sulfate-Reducing Bacteria

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

Study on Erosion-Corrosion Mechanism of B10 Cu-Ni Alloy in Seawater

Corrosion Behavior of High Strength C71500 Cu-Ni Alloy Pipe in Simulated High Sulfide Polluted Seawater at Different Temperatures

Corrosion of Carbon Steel Influenced by Anaerobic Biofilm in Natural Seawater